Mémoire de Maîtrise
DOI
10.11606/D.3.2019.tde-30012019-143451
Document
Auteur
Nom complet
Pedro Del Negro Tayer
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2018
Directeur
Jury
Machado, Izabel Fernanda (Président)
Neves, Julio Cesar Klein das
Rego, Ronnie Rodrigo
Titre en portugais
Avaliação de fadiga de contato em materiais para engrenagens utilizando ensaios de rolamento de esfera sobre disco.
Mots-clés en portugais
Engrenagens
Fadiga de contato
Lubrificação
Rolamentos
Resumé en portugais
Um dos possíveis modos de falha em engrenagens é relacionado com o carregamento cíclico e, por consequência, a ocorrência de fadiga. O início da falha por fadiga ocorre devido à intensificadores de tensão e é geralmente observado no pé do dente (fadiga de flexão) ou na região de contato na superfície do dente (fadiga de contato). Experimentos para avaliação da fadiga de contato em engrenagens são geralmente conduzidos em bancadas de teste e tem custos elevados. Um método alternativo de experimentação de fadiga de contato em engrenagens é avaliado neste trabalho, consistindo no rolamento de esferas sobre um plano (corpo de prova). Dois grupos de corpos de prova foram fabricados com características e propriedades superficiais semelhantes às da superfície do dente de engrenagens nas condições: a) sem shot-peening e b) com shot-peening. As diferentes características dos corpos de prova foram testadas utilizando um equipamento desenvolvido em trabalho anterior para avaliar a fadiga de contato de rolamento, que ocorre no diâmetro primitivo das engrenagens. Resultados indicaram a ocorrência de dois mecanismos de falha comumente encontrados em engrenagens: pitting e spalling, entretanto, o equipamento se mostrou incapaz de monitorar a ocorrência de pitting. Ademais, os corpos de prova com shot-peening apresentaram menor resistência à fadiga para as condições testadas, em desacordo com ensaios de bancada anteriores. Algumas hipóteses foram discutidas para prover justificativas relacionadas aos resultados obtidos.
Titre en anglais
Evaluation of contact fatigue in gear materials using ball rolling on disk experiments.
Mots-clés en anglais
Contact fatigue
Gears
Rolling. lubrication
Shot-peening
Resumé en anglais
One of the possible mechanisms of gear failure is related to the cyclic loading and, consequently, the fatigue occurrence. The onset of fatigue failure occurs due to stress intensifiers and it is generally observed on the fillet (bending fatigue) or on the tooth surface contact region (contact fatigue). Gear fatigue evaluation is usually carried out by test rigs, which are expensive. An alternative method of contact fatigue test of gears is evaluated in this work, which consists of balls rolling on a plane (specimen). Two groups of specimens were manufactured to obtain surface characteristics and properties like gears tooth's surface: a) without shot-peening and b) with shot-peening. The different features of specimens were tested by using an in house developed equipment to evaluate the rolling contact fatigue, which occurs on gears on its diametral pitch. Results indicate the occurrence of two failure modes: pitting and spalling, however, the equipment showed to be unable to monitor the occurrence of pitting. Also, the shot-peened group specimens presented lower fatigue life resistance for the analyzed conditions, which are not in agreement with previous rig tests. Some hypotheses were discussed to provide justifications related to the obtained results.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2019-01-31
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.