Dissertação de Mestrado
DOI
10.11606/D.3.2006.tde-31032008-101929
Documento
Autor
Nome completo
Ronaldo Câmara Cozza
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2006
Orientador
Banca examinadora
Souza, Roberto Martins de (Presidente)
Mello, José Daniel Biasoli de
Tanaka, Deniol Katsuki
Título em português
Estudo do comportamento do coeficiente de desgaste e dos modos de desgaste abrasivo em ensaios de desgaste micro-abrasivo.
Palavras-chave em português
Desgaste
Desgaste abrasivo misto
Desgaste abrasivo por riscamento
Desgaste abrasivo por rolamento
Ensaio de desgaste por micro-abrasão
Regime permanente de desgaste
Resumo em português
Esta Dissertação tem por objetivo estudar o comportamento de diferentes materiais sob a ação de desgaste micro-abrasivo. Como parte do trabalho, foi projetada e construída uma máquina de ensaio desgaste por micro-abrasão por esfera rotativa fixa, com configuração mecânica com diferenças em relação às observadas na literatura (Gee et al., 2005). Como corpos-de-prova, foram utilizadas pastilhas intercambiáveis de metal duro (classe P20) e aço ferramenta M2. As esferas foram de aço AISI 1010 cementado e aço AISI 52100 temperado e revenido. Durante os ensaios, foi inserida entre a esfera e o corpo-de-prova uma pasta abrasiva preparada com carbeto de silício preto, com tamanho médio de partícula de 5 µm. Inicialmente, foram realizados ensaios preliminares, com a finalidade de analisar não só o comportamento do equipamento, mas também estudar a transição entre os modos de desgaste que podem ocorrer durante o desgaste micro-abrasivo. A transição entre os modos de desgaste foi estudada em função da carga normal e dos materiais utilizados durante o ensaio. Os resultados obtidos indicaram boa reprodutibilidade do equipamento e coerência com resultados da literatura. Em seguida, em ensaios denominados definitivos, foram pesquisadas as atuações dos modos de desgaste abrasivo e a obtenção do regime permanente de desgaste. Os resultados mostraram que, com a variação da distância de deslizamento, houve alterações nas ocorrências dos modos de desgaste abrasivo. Por outro lado, em alguns ensaios, o coeficiente de desgaste tendeu a permanecer constante, o que caracteriza a obtenção do regime permanente de desgaste. Entretanto, em outros, o coeficiente de desgaste teve uma evolução aleatória com a distância de deslizamento, fornecendo indicativos de que o desgaste não entrou em regime.
Título em inglês
Wear coefficient and wear mode transition study in micro-abrasive wear testing.
Palavras-chave em inglês
Constant regime of wear
Grooving abrasion
Microabrasive wear testing
Mixed-mode abrasion
Rolling abrasion
Wear
Resumo em inglês
This work presents a study on the behavior of different materials under the action of micro-abrasive wear. A micro-abrasive wear testing machine with fixed sphere was designed and constructed, presenting a mechanical configuration with differences with respect to those found in the literature (Gee et al., 2005). M2 tool steel and WC-Co P20 were used as testing specimen materials. Ball materials were cemented AISI 1010 steel and quenched and tempered AISI 52100 steel. During the tests, an abrasive slurry, prepared with black silicon carbide (SiC) particles (average particle size of 5 µm), was supplied to the contact between the specimen and the ball. Initially, preliminary tests were conducted to study the wear mode transitions that can occur during the micro-abrasive wear and to analyze the operational conditions of the equipment. The wear mode transitions were evaluated as a function of the applied normal load and of the materials used. The results indicated good reproducibility and qualitative agreement with those found in the litarature. Later, a new set of tests was conducted, which analyzed the evolution of the abrasive wear modes and the achievement of steady state wear as a function of sliding distance. The results indicated a continuous variation in the abrasive wear modes with sliding distance. Additionally, in some tests, the wear coefficient tended to stabilize in constant value, which characterizes the achievement of steady state regime. However, in other tests, the wear coefficient presented a non constant evolution of wear coefficient with the sliding distance, which denotes that the constant regime of wear was not obtained.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2008-04-07
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
  • COZZA, R, et al. Relationship between test severity and wear mode transition in micro-abrasive wear tests [doi:10.1016/j.wear.2007.01.099]. Wear [online], 2007, vol. 263, n. -5, p. 111-116.