Thèse de Doctorat
DOI
https://doi.org/10.11606/T.3.2016.tde-31052016-093445
Document
Auteur
Nom complet
Adalto de Farias
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2015
Directeur
Jury
Batalha, Gilmar Ferreira (Président)
Fogagnolo, João Batista
Lima, Milton Sergio Fernandes de
Stipkovic Filho, Marco
Travessa, Dilermando Nagle
Titre en portugais
Avaliação do processamento por atrito linear em chapas da liga de titânio Ti-6Al-4V.
Mots-clés en portugais
ARCAN
Chapas
Ensaio biaxial
Ligas leves
Processamento por atrito linear
Solda por atrito linear
Titânio
Resumé en portugais
Esta tese tem por objetivo a aplicação do processamento por atrito linear na liga de titânio Ti-6Al-4V. Derivado da solda por atrito linear, é um processo recente desenvolvido na década de 90 para união de alumínio. Sua aplicação em outros tipos de materiais como aços e ligas de alto desempenho, em especial o titânio, tem interessado a industria. A metodologia utilizada nesta tese para avaliar o processamento por atrito linear, consistiu na execução de ensaios mecânicos de tração em condições mistas em chapas da liga de titânio Ti-6Al-4V. A máquina utilizada para o processamento das chapas foi um centro de usinagem CNC convencional, adaptado com dispositivos especiais. Além dos ensaios de tração em condições mistas, foram executadas medições de microdurezas nas regiões atingidas pelo processo, avaliação das microestruturas resultantes e medições de tensão residual para uma caracterização mais ampla do processo. As microestruturas na região processada são caracterizadas por uma estrutura totalmente transformada. As temperaturas de pico na região processada excederam a temperatura -transus durante o processamento e a transformação da fase + ocorreu durante a fase de resfriamento. A transformação da fase para resultou na formação de agulhas de fase nos contornos e pelo interior dos grãos da fase . Pequenas regiões com estrutura equiaxial de grãos ( globular) foram observados na zona de processamento. A abordagem dos resultados quantitativos foi feita de forma estatística, visando identificar os parâmetros de maior interação com os resultados observados. Foi identificado nesta tese que a rotação da ferramenta apresentou a maior influência nos resultados de tensão residual, microdureza e tensão de escoamento. Uma importante contribuição à modelagem da tensão de escoamento para materiais anisotrópicos é proposta, baseado em um critério de escoamento ortotrópico. Equações complementares baseadas nos testes mistos de tração e cisalhamento são propostas para modificar o modelo ortotrópico. O intuito deste modelo é indicar em que condições o material tem seu regime de escoamento atingido, podendo servir de base para simulações práticas de peças em condições similares.
Titre en anglais
Evaluation of friction stir processed titatnium Ti-6AI-4V sheets.
Mots-clés en anglais
ARCAN
Biaxial testing
Evaluation of friction stir processed
Formability
Friction stir welding
Titanium
Resumé en anglais
This thesis aims at the application of friction stir processing (FSP) in Ti-6Al-4V titanium alloy. Derived from friction stir welding (FSW), it is a recent process developed in the 90s for aluminum joining. Its application to other types of materials such as steel and high performance alloys, in particular titanium, has interested industry. The methodology applied in this thesis to evaluate FSP, consisted in the execution of tensile test at mixed conditions to Ti-6Al-4V sheets 4. The machine used for processing the sheet was a conventional CNC milling machine, assembled with special fixture devices. In addition to tensile tests, measurements have been performed to the regions affected by the process such as evaluation of microhardness, microstructure and residual stress condition. The microstructures at the processed region are characterized by a transformed structure. The peak temperatures, in the processed region, exceeded the -transus temperature during the processing and transformation of the phase + occurred during the cooling phase. This transformation resulted in the formation of boundary and intergranular phase (Widmanstätten) at the grains. Small regions of equiaxed grain structure (globular ) were observed in the processed zone. The approach to the quantitative results was made in statistical form aiming to identify the parameters interaction with the observed results. It was identified in this thesis that the tool spinning rotation showed the highest influence on the results of residual stress, hardness and yield strength. An important contribution to the modeling of anisotropic materials yield stress is proposed based on an orthotropic yield criterion. Additional equations based on the mixed tests for tensile and shear are proposed to modify the orthotropic model. The purpose of this model is to indicate the conditions under which the material has reached its yield regime, and may be a basis for practical simulations in similar conditions.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-06-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.