Disertación de Maestría
DOI
10.11606/D.3.2006.tde-05092006-122052
Documento
Autor
Nombre completo
Daniel Verga Boeri
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2006
Director
Tribunal
Adamowski, Julio Cezar (Presidente)
Almeida, Sergio Frascino Muller de
Silva, Emilio Carlos Nelli
Título en portugués
Caracterização de materiais compostos por ultra-som.
Palabras clave en portugués
caracterização de materiais
constantes elásticas
ensaios não-destrutivos
fibra de vidro
materiais compostos
ultra-som
Resumen en portugués
Este trabalho apresenta duas técnicas de ensaios não-destrutivos por ultra-som realizados em um tanque com água para determinar as constantes elásticas de materiais compostos de fibra de vidro/epóxi. A primeira técnica é a transmissão direta utilizando um par de transdutores. A segunda é a técnica de pulso-eco, utilizando um único transdutor. A água do tanque atua como um acoplante para transferir a energia mecânica do transdutor para a amostra. Como o transdutor não fica em contato direto com a amostra, pode-se garantir um acoplamento constante. O sistema de medição dota de um dispositivo que permite medir a velocidade da onda elástica sob diferentes ângulos de incidência, através da rotação manual da amostra. Devido ao fenômeno de conversão de modos com incidência oblíqua na interface amostra-água, ensaios por ultra-som em tanques com água fornecem as informações necessárias para o cálculo das constantes elásticas em amostras de materiais anisotrópicos, numa dada direção, a partir das medições das velocidades longitudinal e de cisalhamento. Numa dada direção de propagação em um meio anisotrópico, existem três ondas elásticas distintas: uma longitudinal e duas de cisalhamento. Se as constantes elásticas do material são conhecidas, é possível obter as três velocidades em uma dada direção bastando resolver a equação de Christoffel. Invertendo a equação de Christoffel, obtém-se as constantes elásticas a partir das velocidades medidas em uma dada direção. Os experimentos são realizados com amostras de fibra de vidro/epóxi unidirecionais e bidirecionais, utilizando transdutores com freqüências de 0,5 MHz, 1 MHz e 2,25 MHz. Os resultados experimentais obtidos utilizando ambas as técnicas são comparados com um modelo denominado “Regra das Misturas” e com resultados da literatura.
Título en inglés
Ultrasonic characterization of composite materials.
Palabras clave en inglés
composite materials
elastic constants
fiber reinforced composites
material characterization
nondestructive testing
ultrasonic
Resumen en inglés
In this work, two ultrasonic non destructive techniques were implemented in a water tank and used to determine the elastic constants of glass-epoxy composites samples. The first is the through-transmission technique implemented with a pair of ultrasonic transducers. The second is the back-reflection technique that uses a single transducer in pulse-eco mode. The water acts as a couplant and transfers the mechanical energy from the transducer to the sample. As the transducer is not in direct contact with the sample, we can guarantee a good coupling with the immersion technique. With the system device, it is possible to measure the velocities of the elastic waves in different angles by manually rotating the sample. Due to wave mode conversion phenomenon at the sample-water interface with oblique incidence, ultrasonic immersion testing provides information to calculate the elastic constants of the specimen by measuring longitudinal and shear wave speeds. There are three different modes of waves, one longitudinal and two shear waves, for any given direction of propagation in an anisotropic medium. If the elastic constants of a medium are known, it is possible to obtain the three wave speeds in particular propagations directions by solving the Christoffel equation. Inverting the Christoffel equation, it is possible to obtain the elastic constants from the measured wave speed in several specific directions of the anisotropic material. Measurements were carried out on unidirectional and bidirectional glass-epoxy composite samples, using transducers with central frequency of 0.5 MHz, 1 MHz, and 2.25 MHz. The experimental results obtained with both techniques are compared with a model denominated “Rule of Mixture” estimation and with the literature.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2006-09-13
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.