Disertación de Maestría
DOI
https://doi.org/10.11606/D.3.2017.tde-14032017-133434
Documento
Autor
Nombre completo
Dan Yamashita
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2016
Director
Tribunal
Adamowski, Julio Cezar (Presidente)
Almeida, Sergio Frascino Muller de
Alvarez, Nicolás Leonardo Pérez
Título en portugués
Determinação das propriedades elásticas de laminados compósitos carbono/epóxi pelo método de ultrassom por imersão.
Palabras clave en portugués
Constante elástica
Materiais compósitos
Ultrassom
Resumen en portugués
Este trabalho tem o objetivo de determinar as constantes elásticas de laminados compósitos de carbono/epóxi através do método não destrutivo de ultrassom, utilizando a técnica da imersão. Foram implementados dois métodos de imersão em água para a determinação das constantes elásticas. Um que utiliza o percurso na água sem a amostra como referência (FRM), e outro que utiliza o percurso com incidência normal na amostra como referência (SRM). Laminados unidirecionais e biaxiais foram ensaiados em um goniômetro com elevada precisão de movimento angular, e a aquisição de sinais feita com alta taxa de amostragem e grande resolução de amplitude. Uma análise da influência da variação da temperatura e espessura foi feita e comprovada a superioridade do método SRM sobre o FRM. A compensação da temperatura através de um par de transdutores, bem como através de um termômetro com resolução de 0.01°C foi implementada e comparada. As curvas de velocidade foram obtidas com transdutores de diferentes frequências centrais e comparadas. Foi realizada uma análise detalhada da sensibilidade das constantes elásticas com relação as velocidades em cada plano de medição, e através desta análise foram utilizados os planos mais adequados para reconstrução das constantes elásticas. Também foi verificada a polarização das ondas de cisalhamento para cada plano de medição, uma vez que é necessária a correta associação da velocidade experimental com a velocidade calculada para o procedimento de otimização. Um algoritmo de otimização foi utilizado para reconstruir as constantes elásticas dos laminados compósitos a partir da medição experimental das velocidades, onde foi avaliada a convergência utilizando a equação de Christoffel na forma implícita e explícita, para os materiais de simetria tetragonal e hexagonal.
Título en inglés
Determination of elastic properties of carbon/epoxy composite laminates by immersion ultrasonic method.
Palabras clave en inglés
Composite materials
Elastic constant
Ultrasonic
Resumen en inglés
The objective of this work is to obtain the elastic constants of carbon/epoxy composite laminates using ultrasonic non destructive testing, with immersion technique. Two immersion methods were implemented. One method uses as reference the path without sample, called fluid reference method (FRM), the second method uses the path with the specimen in normal incidence, called self-reference method (SRM). Unidirectional and biaxial laminates were tested using a goniometer with high angular resolution, and the signals were acquired with a high sample rate and amplitude resolution. Analyses of the influence of temperature and thickness variations were performed and concluded the superiority of the SRM over the FRM method. Temperature compensation using a pair of transducers and a 0.01° resolution thermometer was implemented and compared. Velocity curves were obtained and compared using transducers with different frequencies. A detailed analysis was performed to evaluate the sensitivity of the elastic constants to each velocity in different acquisition planes, and the results were used to reconstruct the elastic constants in the planes/velocities which they were most sensible to. As the correct association of each experimental velocity with the calculated velocities from Christoffel's equation is necessary, an analysis of the polarization mode of each velocity in the acquisition planes was also performed. An optimization algorithm was used to reconstruct the elastic constants of composite laminates from experimental velocities. Its convergence was evaluated for the implicit and explicit form of Christoffel's equation, and for materials with tetragonal and hexagonal symmetry.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-03-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.