Tesis Doctoral
DOI
10.11606/T.43.2000.tde-02122013-185104
Documento
Autor
Nombre completo
Cezar Soares Martins
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2000
Director
Tribunal
Missell, Frank Patrick (Presidente)
Jardim, Renato de Figueiredo
Knobel, Marcelo
Machado, Fernando Luís de Araújo
Petrilli, Helena Maria
Título en portugués
Magnetização e Magnetoresistência Gigante em Ligas Granulares CuNiFe
Palabras clave en portugués
Magnetismo (propriedades magnéticas)
Matéria condensada
Resumen en portugués
Neste trabalho, estudamos as propriedades magnéticas e a magnetoresistência gigante (GMR) em fitas de Cu IND.80 Ni IND.20-xFe IND.x (x = 2,5 ; 5; 10; 17, 5; 20) produzidas por melt-spinning. As fitas foram estudadas como função da temperatura de tratamento térmico T IND.an 500°C, usando-se um magnetômetro SQUID. Uma grande variedade de estruturas granulares foram obtidas para diferentes razões de Ni/Fe e condições de tratamento térmico. Para Cu80 Ni10 Fe10, a magnetização não apresentou histerese mensurável para T 50K. Este comportamento é consistente com as curvas de susceptibilidade que indicam uma temperatura de bloqueio abaixo de 50K. Nesta temperatura, o maior valor da GMR(19%) foi obtido para as fitas tratadas a 400°C por duas horas. As curvas de magnetização foram comparadas a um modelo teórico que assume uma distribuição de momentos magnéticos. Para Cu80Ni15Fe5,a microestrutura e as propriedades magnéticas são muito sensíveis ao tratamento térmico. Para as ligas com composições 10; 15; 17,5% de Fe, a magnetização de saturação apresentou uma redução com o tratamento a 400°C. Esta redução foi explicada através da formação de partículas perto da região Invar. Um comportamento anômalo linear da amplitude da magnetoresistência foi observado e explicado pelo espalhamento dependente do spin, que acontece quando um elétron se move de uma partícula superparamagnética para uma partícula bloqueada termicamente.
Título en inglés
Magnetization and giant magnetoresistance in granular alloys CuNiFe.
Palabras clave en inglés
Condensed matter
Magnetism (magnetic properties)
Resumen en inglés
In this work, we study the magnetic properties and giant magnetoresistance (GMR) in ribbons of Cu80 Ni20-xFex (x = 2.5, 5, 10, 17.5, 20) prepared by melt-spinning. The ribbons were studied as a function of annealing temperature Tan 500°C, using a SQUID magnetometer. A wide variety of granular structures é obtained for different Ni/ Fe ratios and annealing conditions. In Cu80 Ni10 Fe10 , the magnetization shows no static hysteresis for T 50K. This behaviour is consistent with the susceptibility curve which indicates a blocking temperature below 50K. At this temperature, the largest GMR value was obtained for the ribbons annealed at 400°C for two hours. The magnetization curves were compared with a theoretical model that takes into account the magnetic moment distribution. In Cu80 Ni15Fe5, the microstructure and magnetic properties are much more sensitive to annealing. For t he ribbons with 10, 15, 17.5 % Fe composition, the magnetization presented a reduction with annealing at 400°C. This redution may be explained in terms of particle formation near the Invar region. An anomalous linear behaviour of the MR was observed and can be explained in terms of spin-dependent scattering when an electron passes from a superparamagnetic particle to a thermally blocked particle.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-02-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.