Tesis Doctoral
DOI
10.11606/T.43.1985.tde-05122013-143657
Documento
Autor
Nombre completo
Klemensas Rimgaudas Juraitis
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1985
Director
Tribunal
Sano, Walter (Presidente)
Oliveira, Mario Jose de
Paduan Filho, Armando
Qualifik, Paul
Rettori, Carlos
Título en portugués
Estudo da transição da fase estrutural do cloreto de níquel dihidratado com diferentes técnicas experimentais
Palabras clave en portugués
Física do estado sólido
Resumen en portugués
Estudamos através de varias técnicas experimentais a transição de fase estrutural do clorêto de níquel dihidratado. A temperatura de transição foi determinada através da técnica de calor específico a (222 ± 1) K. Através das técnicas de análise térmica diferencial, RPE e dilatometria, mostramos que há uma histerese de 20k. As medidas de condutividade elétrica indicam que esta substância tem as propriedades de um cristal quase-unidimensional, apresentando uma alta anisotropia na condução ao longo de seus eixos cristalinos. Na variação da temperatura a condutividade apresentou uma transição do tipo metal-isolante, que pode ser atribuída à instabilidade de Peierls. Todas as técnicas acima descritas, menos a de RPE, foram especialmente desenvolvidas para o presente trabalho.
Título en inglés
A study of the structural phase transition in nickel chloride dihydrate with different experimental techniques
Palabras clave en inglés
Solid state physics
Resumen en inglés
Structural phase transition of di-hydrated nickel chloride has been studied with several experimental techniques. The transition temperature was determined at (222 ± 1) K with specific heat rneasurement. Using differential thermal analysis, EPR and dilatometric techniques a hysteresis of 20 K has been determined in this transition. Electric conductivity measurement indicated that this substance has properties of quasi-unidimensional crystal with high anisotropic conductivity along the needle axis and its temperature variation has shown that it go to a metal-insulator transition probably due to a Peierls like instability. All the above techniques, except EPR, have been developed specially for the present work.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-02-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.