Disertación de Maestría
DOI
https://doi.org/10.11606/D.43.2017.tde-13032017-121314
Documento
Autor
Nombre completo
Marcelo Jacob da Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1999
Director
Título en portugués
Crescimento e Caracterização de Pontos Quânticos de InAs Auto-formados
Palabras clave en portugués
Matéria Condensada ; Semicondutores
Resumen en portugués
Neste trabalho, estudamos o crescimento epitaxial por feixe molecular de pontos quânticos de InAs/GaAs, bem como sua propriedades ópticas e morfológicas. O método de crescimento, em baixa taxa foi usado para a fabricação de estruturas de pontos quânticos com alturas médias suficientes para a obtenção de resposta óptica nas faixas de 1,3'mü'm e 1,5'mü'm em temperatura ambiente. O interesse na manufatura desse tipo de amostra decorre do fato de serem estes os comprimento de onda de mínima atenuação de sinal em redes de transmissão por fibras ópticas. O estudo sistemático das etapas envolvidas na evolução de pontos quânticos de superfície no regime de baixa taxa de deposição permitiu entender como tais estruturas, com alturas médias bem maiores que as normalmente obtidas na literatura, puderam ser alcançadas. As condições de crescimento foram otimizadas para a produção de emissões estreitas nas faixas de comprimento de onda
Título en inglés
Study of the tuning of optical emission of InAs / GaAs quantum dots in the 1,3'mü'm and 1,5'mü'm regions
Palabras clave en inglés
Condensed matter
semiconductors
Resumen en inglés
In this work, we studied the evolution of InAs quantum dots grown by MBE as a function o f the amount o f material deposited. The monitoring o f the quantum-dot prope1ties during their evolution was possible because of the growth of a sample in which the thickness o f material was varied continuously on its area. The structure o f the samples used in this work consists oftwo quantmn-dot layers, one on the samples' surface and the other between GaAs barriers. The first quantum-dot layer was used in the morphological characterization, through AFM images, and the second one was probed by photoluminescense measurements. Moreover, the structure includes an InxGa1_xAs quantum well to be used as a reference. The possibility of carrying out optical and morphological measurements on the same sample provided us with a way to make comparisons between the topographical and optical features, yielding some interesting results, as the dependence of the optical emission with the surface quantum-dot coverage and its degradation when the islands density is higher than 1 ÜÜÜJ.Lm-2
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
29823_SILVA.pdf (14.45 Mbytes)
Fecha de Publicación
2017-03-13
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.