Dissertação de Mestrado
DOI
10.11606/D.43.2017.tde-13032017-121314
Documento
Autor
Nome completo
Marcelo Jacob da Silva
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 1999
Orientador
Título em português
Crescimento e Caracterização de Pontos Quânticos de InAs Auto-formados
Palavras-chave em português
Matéria Condensada ; Semicondutores
Resumo em português
Neste trabalho, estudamos o crescimento epitaxial por feixe molecular de pontos quânticos de InAs/GaAs, bem como sua propriedades ópticas e morfológicas. O método de crescimento, em baixa taxa foi usado para a fabricação de estruturas de pontos quânticos com alturas médias suficientes para a obtenção de resposta óptica nas faixas de 1,3'mü'm e 1,5'mü'm em temperatura ambiente. O interesse na manufatura desse tipo de amostra decorre do fato de serem estes os comprimento de onda de mínima atenuação de sinal em redes de transmissão por fibras ópticas. O estudo sistemático das etapas envolvidas na evolução de pontos quânticos de superfície no regime de baixa taxa de deposição permitiu entender como tais estruturas, com alturas médias bem maiores que as normalmente obtidas na literatura, puderam ser alcançadas. As condições de crescimento foram otimizadas para a produção de emissões estreitas nas faixas de comprimento de onda
Título em inglês
Study of the tuning of optical emission of InAs / GaAs quantum dots in the 1,3'mü'm and 1,5'mü'm regions
Palavras-chave em inglês
Condensed matter
semiconductors
Resumo em inglês
In this work, we studied the evolution of InAs quantum dots grown by MBE as a function o f the amount o f material deposited. The monitoring o f the quantum-dot prope1ties during their evolution was possible because of the growth of a sample in which the thickness o f material was varied continuously on its area. The structure o f the samples used in this work consists oftwo quantmn-dot layers, one on the samples' surface and the other between GaAs barriers. The first quantum-dot layer was used in the morphological characterization, through AFM images, and the second one was probed by photoluminescense measurements. Moreover, the structure includes an InxGa1_xAs quantum well to be used as a reference. The possibility of carrying out optical and morphological measurements on the same sample provided us with a way to make comparisons between the topographical and optical features, yielding some interesting results, as the dependence of the optical emission with the surface quantum-dot coverage and its degradation when the islands density is higher than 1 ÜÜÜJ.Lm-2
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
29823_SILVA.pdf (14.45 Mbytes)
Data de Publicação
2017-03-13
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.