Tesis Doctoral
DOI
10.11606/T.43.1998.tde-30082012-153600
Documento
Autor
Nombre completo
Daniel Reinaldo Cornejo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1998
Director
Tribunal
Missell, Frank Patrick (Presidente)
Becerra, Carlos Castilla
Cardoso, Jose Roberto
Guimarães Filho, Alberto Passos
Landgraf, Fernando Jose Gomes
Título en portugués
Aplicação do Modelo de Preisach em Ímãs Nanocristalinos
Palabras clave en portugués
Efeito exchang-spring
Imãs nanoestruturados
Modelagem de histerese
Modelo de Preisach
Resumen en portugués
Estudamos propriedades magnéticas de ligas nano cristalinas de Sm-F e-Co. As ligas foram preparadas por mecano-síntese e posterior tratamento térmico. Como resultado, obtivemos ímãs nanocristalinos de Sm18 (Fe,Co)82 , com Sm(Fe,Co)7 como fase principal. As ligas apresentaram excelentes propriedades magnéticas: remanências relativas Mn/ Ms ~ 0.6 e coercividades na faixa 5-20 kOe, dependendo do teor de Fe nos materiais. Interações magnéticas nas ligas foram estudadas com base nos gráficos ele Henkel. Interpretamos, nestes gráficos, de maneira consistente a influência elas interações e dos estados desmagnetizados.
Título en inglés
Application of Preisach model in nanocrystalline magnets
Palabras clave en inglés
Exchange-spring behavior
Modeling of hysteresis
Nanostructures magnets
Preisach model
Resumen en inglés
We studied the magnetic properties of nanocrystalline Sm-Fe-Co alloys. These alloys were prepared by mechanical alloying and subsequent annealing. We obtained nanocrystalline rnagnets of composition Sm18 (Fe, Co )82 , for which the main hard magnetic phase is Sm(Fe, Co)82. The alloys showed excellent magnetic properties: relative remanence Mn/ Ms :2; 0.6 and coercive fields ranging from 5 to 20 k0e, depending upon the amount of Fe present. Henkel plots were used in order to study magnetic interactions in these alloys. The influence of the interactions and the demagnetized state on the Henkel plots was also studied.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
45415Cornejo.pdf (5.82 Mbytes)
Fecha de Publicación
2012-08-31
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.