Tesis Doctoral
DOI
10.11606/T.43.2001.tde-05072012-171055
Documento
Autor
Nombre completo
Adriana Pedrosa Biscaia Tufaile
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2001
Director
Tribunal
Santos, Antonio Domingues dos (Presidente)
Brasil, Maria José Santos Pompeu
Macedo, Waldemar Augusto de Almeida
Oliveira, Mario Jose de
Rechenberg, Hercilio Rodolfo
Título en portugués
Efeito Kerr magneto-óptico espectral e sperimagnetismo de filmes amorfos de terra rara-Co
Palabras clave en portugués
Efeitos Kerr magneto-ópticos
Figura de mérito
Filmes amorfos de terra rara-Co
Modulação de fase
Sperimagnetismp
Resumen en portugués
Observamos o comportamento espectral do efeito Kerr transversal, para filmes amorfos de terra rara - cobalto na região do espectro visível e ultravioleta próximo (comprimento de onda, , entre 325 nm e 670 nm), onde o sinal magnetoóptico apresentou um máximo na região azul do espectro. Concluímos que, para esta região espectral, a variação relativa de refletividade é proporcional à magnetização do cobalto e a constante de proporcionalidade depende da composição da liga e do comprimento de onda da luz. Desenvolvemos uma técnica de modulação de fase, própria para medir o efeito Kerr transversal e a comparamos com a técnica de modulação de amplitude. Montamos um magnetômetro a efeito Kerr que opera com a modulação de fase e utiliza um laser de He-Cd ( = 325 nm e 442 nm) ou um diodo laser vermelho ( = 670 nm). Fazendo uma analogia com a figura de mérito para os efeitos Kerr longitudinal e polar (Fe), nós propusemos uma figura de mérito para o efeito Kerr transversal (FJ. Mostramos que sua dependência do ângulo de incidência é semelhante à da variação relativa de refletividade e, comparando medidas da figura de mérito do efeito Kerr longitudinal com a figura de mérito para o efeito transversal, comprovamos que a grandeza proposta é um bom parâmetro para medida de qualidade magnetoóptica de materiais. Observamos os efeitos do sperimagnetismo de ligas com anisotropia local fraca (Gd-Co) e forte (Ho-Co), através do comportamento térmico dos ciclos de histerese magnética e magnetoóptica. Dentre os fenômenos observados estão os efeitos da compensação, o crescimento hiperbólico do campo coercivo e os efeitos da reorientação de spin. Para a liga de Gd20C080a, transição observada foi uma inversão de spin, cujo o campo magnético aplicado, no qual ocorre a transição, cresce exponencialmente com o aumento da temperatura da amostra.
Título en inglés
Spectral magneto-optical Kerr effect and magnetism-speri of the films of amorphous rare earth-Co
Palabras clave en inglés
Figure of merit
magnetism-Speri
Magneto-optical Kerr effect
Movies amorphous rare earth-Co phase modulation
Resumen en inglés
We have observed the spectral behavior of the transverse magnetooptical Kerr effect (TMOKE) in thin films of rare earth - cobalt amorphous alloys for the visible and the near-ultraviolet ranges of spectrurn (wavelength fiom 325 nm up to 670 nm). The relative change of reflectivity has shown a maximum at the blue wavelength. We have concluded that this magneto-optical signal is proportional to the cobalt magnetization and the proportionality constant depends on the alloy composition and on the wavelength. Besides developing an apparatus and a new phase modulation technique for the TMOKE, we have compared it to the more usual amplitude modulation TMOKE technique. This apparatus operates using either a He-Cd laser ( = 325 nm and 442 nm) for a red diode laser ( = 670nm). We have proposed the figure of merit for the transverse Kerr effect (F,) by analogy with the figure of merit for the longitudinal and polar Kerr effect (Fe). We have measured F, as a function of the angle of incidence and we have shown that F, has the same behavior of the magneto-optical signal. A comparison between F, and Fe has shown that F, is as good parameter as well as Fe for the characterization of the materials magneto-optical quality. We have studied the sperimagnetism of thin films of amorphous alloys with weak (Gd-Co) and strong (Ho-Co) random local anisotropy by the thermal behavior of the magnetic and magneto-optical hysteresis loops. The phenomena of compensation, coercivity and spin-reorientation phase transitions were observed. The comparison between magnetic and magneto-optical hysteresis loops for Gd20C~8h0as shown that the transition occurs from a colinear phase to an opposite collinear phase. In this case, the transition magnetic field grows exponentially when the temperature increases.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
33413Tufaile.pdf (1.24 Mbytes)
Fecha de Publicación
2012-07-05
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.