Tesis Doctoral
DOI
10.11606/T.43.2011.tde-29092011-170342
Documento
Autor
Nombre completo
Jim Heiji Aburaya
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2011
Director
Tribunal
Tabacniks, Manfredo Harri (Presidente)
Chubaci, Jose Fernando Diniz
Dagli, Maria Lucia Zaidan
Partiti, Carmen Silvia de Moya
Zoppa, André Luis do Valle de
Título en portugués
Modificação superficial de titânio para promoção de osteointegração
Palabras clave en portugués
Biomaterial
Células em cultura
Íons
Titânio
Resumen en portugués
O titânio é considerado um biomaterial (material biocompatível) pela baixa reatividade e pela grande estabilidade da sua camada de óxido superficial. Pelas suas propriedades mecânicas ele é usualmente utilizado na fabricação de substitutos ósseos e implantes dentários. Visando contribuir para o desenvolvimento de novas superfícies osteointegráveis, neste trabalho foram estudadas duas superfícies de titânio modificadas com implantação iônica de P e BF2 com energia de 30 e 77keV, respectivamente. As superfícies foram submetidas a ensaios in vitro de cultura celular de células osteoblásticas (MG-63) e os resultados foram comparados com duas superfícies comerciais: poliestireno tratado para meio de cultura celular (PC) e titânio comum utilizado em implante dentário (TI). A atividade enzimática da fosfatase alcalina (FA) associadas à formação de biofilme mineralizado pelas células diferenciadas foram avaliadas. Concentrações de cálcio e fósforo no biofilme foram determinadas por espectroscopia de raios-X induzida por prótons, PIXE. Imagens superficiais com microscopia eletrônica de varredura serviram para verificar a homogeneidade e integridade dos biofilmes formados. Medidas de ângulo de contato foram realizadas para determinar o caráter hidrofílico das superfícies e do biofilme formado. As superfícies PC e TI se apresentaram hidrofílicas com formação de biofilme menos homogêneo que as apresentadas pelas superfícies PT e BFT, ambas hidrofóbicas. As concentrações de FA medidas no meio de cultura indicaram consumo maior que a secreção em PC e TI. Em PT e BFT foram observados acúmulos de FA no meio de cultura. Concentrações maiores de cálcio e fósforo foram observadas em PC e TI. Destas observações, as quatro superfícies podem ser consideradas biocompatíveis (não citotóxicas) pela formação de biofilme mineralizado e pelas medidas de atividade enzimática.
Título en inglés
Titanium modification for the promotion of osteointegration
Palabras clave en inglés
Biomaterial
Cell culture
Ion implantation
Titanium
Resumen en inglés
Titanium is considered a biomaterial (biocompatible material) due to its low reactivity and the great stability of its surface native oxide layer. With excellent mechanical properties, titanium is widely used as bone substitutes and dental implants. Aiming to contribute for the development of new surfaces to promote osteoblastic cell grow, two ion-beam-modified titanium samples were compared with two commercially available surfaces: polystyrene treated for cellular cultures (PC), and regular titanium used in dental implants (TI). The modified titanium samples were ion beam implanted with 30 and 77 keV phosphorous and BF2, respectively. All surfaces were employed for in vitro assays using cultures of osteoblastic cells (MG-63). The Phosphatase Alkaline Enzymatic Activity (ALP) was measured and associated with the mineralized bio-film formed by the differentiated cells. The concentration of calcium and phosphorus in the mineralized bio-film was measured by Proton Induced X-ray Emission, PIXE. Scanning Electron Microscope images were used to access the bio-film homogeneity and integrity. Contact angle measurements were used to characterize the wettability of the surfaces and the resulting bio-film. In spite of being more hydrophilic, the surfaces PC and TI formed of a less homogeneous bio-film than the PT and BFT surfaces, which were less hydrophilic. The ALP in the cell culture medium indicated greater consumption than secretion for PC and TI, while for PT and BFT accumulation of ALP was observed. Concentrations of calcium and phosphorus were greater for PC and TI samples. The four surfaces can be considered biocompatible (not cytotoxic) due to mineral bio-film formation and enzymatic activity measurements.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Aburaya.pdf (6.83 Mbytes)
Fecha de Publicación
2011-11-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.