• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tesis Doctoral
DOI
10.11606/T.46.2006.tde-07022007-220153
Documento
Autor
Nombre completo
Monica Luisa Chaves de Andrade Afonso
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2006
Director
Tribunal
Agostinho, Silvia Maria Leite (Presidente)
Melo, Hercílio Gomes de
Motheo, Artur de Jesus
Rocha, Sonia Regina Biaggio
Serrano, Silvia Helena Pires
Título en portugués
Caracterização do aço inoxidável austenítico UNS S31254 em meio de NaCI 0,11 mol L-1 visando seu emprego em implantes ortopédicos
Palabras clave en portugués
Aço inoxidável austenítico
Corrosão
Implantes ortopédicos
Soroalbumina bovina
Resumen en portugués
Foi feita a caracterização eletroquímica do aço inoxidável austenítico UNS S31254 em meio de NaCl 0,11 mol L-1 na ausência e presença de soro albumina bovina (BSA) visando seu emprego em implantes ortopédicos. Foram empregadas como técnicas: medidas de potencial de circuito aberto, curvas de polarização, cronoamperometria, EIE, XPS, MEV, EDS e EEO. O comportamento eletroquímico do aço 254 foi comparado com o de outros aços empregados em implantes ortopédicos (ISO 5832-9, ASTM F138, e AISI 316L) na ausência e presença de BSA. O aço 254 se mostrou semelhante ao ISO 5832-9: encontra-se passivado desde o potencial de corrosão até o de transpassivação; a presença de inclusões de óxidos de cálcio e alumínio no aço 254 foi considerada a responsável por um potencial de transpassivação 100 mV menos positivo do que o observado com o aço ISO 5832-9. Foi detectada. além de óxido de Cr(III), a presença de Mo na forma Mo(VI) no filme passivo do aço 254. A ação da BSA, ora passivante ora catalisadora, depende de sua concentração, da natureza do substrato metálico, e do potencial na interfase metal-solução. A BSA modifica o mecanismo de oxidação do aço 254 e inibe seletivamente a dissolução dos seus elementos constituintes, em particular, níquel e cromo.
Título en inglés
Electrochemical characterization of UNS S31254 austenitic stainless steel in 0.11 mol L-1 NaCl medium in order to propose its application in orthopaedic implants
Palabras clave en inglés
Bovine serum albumin
Corrosion
Orthopaedic implants
Stainless steel
Resumen en inglés
The electrochemical characterization of UNS S31254 has been made in 0.11 mol L-1 NaCl medium in the absence and presence of bovine serum albumin (BSA) in order to propose its application in orthopaedic implants. The techniques employed were: open circuit potential measurements, polarization curves, chronoamperometry, EIS, XPS, SEM, EDS and EEO. The electrochemical behavior of 254 SS was compared to that observed for ISO 5832-9, ASTM F138 and AISI 316L stainless steels, used in orthopedic implants, in the absence and presence of BSA. 254 SS is similar to ISO 5832-9 SS: it is passivated on the potential range between the corrosion and the transpassivation potentials; the presence of calcium and aluminum oxides can be responsible for the shift of about 100 mV to less positive potentials on the transpassivation potential when compared to ISO 5832-9 SS. The presence of Mo(VI) was detected beside Cr(III) as passivating film for 254 SS. BSA action depends on its concentration, the nature of the metallic substract and on the potential in the metal-solution interphase. BSA changes the oxidation mechanism of 254 SS and promotes the selective dissolution of the elements particularly nickel and chromium.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
capa.pdf (5.81 Kbytes)
parte1.pdf (12.22 Kbytes)
parte2.pdf (54.19 Kbytes)
parte3.pdf (374.43 Kbytes)
parte4.pdf (94.11 Kbytes)
parte5.pdf (416.91 Kbytes)
parte6.pdf (663.57 Kbytes)
parte7.pdf (421.81 Kbytes)
parte8.pdf (44.60 Kbytes)
Fecha de Publicación
2007-03-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.