• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Thèse de Doctorat
DOI
10.11606/T.46.2006.tde-07022007-220153
Document
Auteur
Nom complet
Monica Luisa Chaves de Andrade Afonso
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2006
Directeur
Jury
Agostinho, Silvia Maria Leite (Président)
Melo, Hercílio Gomes de
Motheo, Artur de Jesus
Rocha, Sonia Regina Biaggio
Serrano, Silvia Helena Pires
Titre en portugais
Caracterização do aço inoxidável austenítico UNS S31254 em meio de NaCI 0,11 mol L-1 visando seu emprego em implantes ortopédicos
Mots-clés en portugais
Aço inoxidável austenítico
Corrosão
Implantes ortopédicos
Soroalbumina bovina
Resumé en portugais
Foi feita a caracterização eletroquímica do aço inoxidável austenítico UNS S31254 em meio de NaCl 0,11 mol L-1 na ausência e presença de soro albumina bovina (BSA) visando seu emprego em implantes ortopédicos. Foram empregadas como técnicas: medidas de potencial de circuito aberto, curvas de polarização, cronoamperometria, EIE, XPS, MEV, EDS e EEO. O comportamento eletroquímico do aço 254 foi comparado com o de outros aços empregados em implantes ortopédicos (ISO 5832-9, ASTM F138, e AISI 316L) na ausência e presença de BSA. O aço 254 se mostrou semelhante ao ISO 5832-9: encontra-se passivado desde o potencial de corrosão até o de transpassivação; a presença de inclusões de óxidos de cálcio e alumínio no aço 254 foi considerada a responsável por um potencial de transpassivação 100 mV menos positivo do que o observado com o aço ISO 5832-9. Foi detectada. além de óxido de Cr(III), a presença de Mo na forma Mo(VI) no filme passivo do aço 254. A ação da BSA, ora passivante ora catalisadora, depende de sua concentração, da natureza do substrato metálico, e do potencial na interfase metal-solução. A BSA modifica o mecanismo de oxidação do aço 254 e inibe seletivamente a dissolução dos seus elementos constituintes, em particular, níquel e cromo.
Titre en anglais
Electrochemical characterization of UNS S31254 austenitic stainless steel in 0.11 mol L-1 NaCl medium in order to propose its application in orthopaedic implants
Mots-clés en anglais
Bovine serum albumin
Corrosion
Orthopaedic implants
Stainless steel
Resumé en anglais
The electrochemical characterization of UNS S31254 has been made in 0.11 mol L-1 NaCl medium in the absence and presence of bovine serum albumin (BSA) in order to propose its application in orthopaedic implants. The techniques employed were: open circuit potential measurements, polarization curves, chronoamperometry, EIS, XPS, SEM, EDS and EEO. The electrochemical behavior of 254 SS was compared to that observed for ISO 5832-9, ASTM F138 and AISI 316L stainless steels, used in orthopedic implants, in the absence and presence of BSA. 254 SS is similar to ISO 5832-9 SS: it is passivated on the potential range between the corrosion and the transpassivation potentials; the presence of calcium and aluminum oxides can be responsible for the shift of about 100 mV to less positive potentials on the transpassivation potential when compared to ISO 5832-9 SS. The presence of Mo(VI) was detected beside Cr(III) as passivating film for 254 SS. BSA action depends on its concentration, the nature of the metallic substract and on the potential in the metal-solution interphase. BSA changes the oxidation mechanism of 254 SS and promotes the selective dissolution of the elements particularly nickel and chromium.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
capa.pdf (5.81 Kbytes)
parte1.pdf (12.22 Kbytes)
parte2.pdf (54.19 Kbytes)
parte3.pdf (374.43 Kbytes)
parte4.pdf (94.11 Kbytes)
parte5.pdf (416.91 Kbytes)
parte6.pdf (663.57 Kbytes)
parte7.pdf (421.81 Kbytes)
parte8.pdf (44.60 Kbytes)
Date de Publication
2007-03-20
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.