Tesis Doctoral
DOI
10.11606/T.46.2009.tde-10122009-113135
Documento
Autor
Nombre completo
Jorge Amim Júnior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Petri, Denise Freitas Siqueira (Presidente)
Campana Filho, Sérgio Paulo
Kawano, Yoshio
Salvadori, Maria Cecília Barbosa da Silveira
Soldi, Valdir
Título en portugués
Caracterização e aplicação de filmes finos de acetato butirato carboximetil celulose
Palabras clave en portugués
Adsorção de proteínas
AFM
Elipsometria
Energia superficial
Éster de celulose
Resumen en portugués
Esta tese apresenta o estudo do efeito do solvente acetato de etila e acetona no comportamento em solução dos polímeros acetato butirato celulose (CAB) e acetato butirato carboximetil celulose (CMCAB) e nas características dos seus filmes finos obtidos pela técnica de revestimento rotacional ou por adsorção. As medidas de viscosidade e espalhamento de raio-X a baixo ângulo (SAXS) mostraram que o acetato de etila é um melhor solvente para CAB e CMCAB do que a acetona. A caracterização dos filmes foi feita através de medidas de elipsometria, microscopia de força atômica (AFM), espectrocospia vibracional por geração de soma de freqüências (SFG) e medidas de ângulo de contato. Os filmes de CMCAB obtidos por revestimento rotacional são mais espessos quando preparado em acetona do que em acetato de etila. Imagens de AFM mostraram que os filmes de CMCAB oriundos de soluções em acetato de etila são mais homogêneos e lisos do que aqueles preparados a partir de acetona. Medidas de SFG comprovaram a forte afinidade da acetona com SiO2/Si, mostrando que esse solvente cria uma nova camada para os filmes de CAB e CMCAB. Os valores de energia superficial calculados para CAB e CMCAB foram semelhantes ~ (49,0 ± 0,5) mJ/m², sendo a contribuição da componente dispersiva maior que a da componente polar. A adsorção das proteínas lisozima, albumina do soro bovino (BSA), concanavalina A e jacalina foram mais pronunciadas sobre os filmes de CMCAB do que sobre CAB. Indicando que a presença do grupo carboximetil (CM) contribui significativamente no processo de adsorção das biomoléculas. O efeito da rugosidade dos filmes de CAB e CMCAB sobre o processo de adsorção das proteínas foi estudado. No caso do CMCAB, a adsorção das proteínas foi mais pronunciada sobre o filme rugoso do que sobre o filme mais liso. Entretanto, para os filmes de CAB a rugosidade não teve um efeito significativo na adsorção das proteínas
Título en inglés
Characterization and application of thin film of carboxymehtylcellulose acetate butyrate
Palabras clave en inglés
AFM
Cellulose ester
Ellipsometry
Protein adsorption
Surface energy
Resumen en inglés
The effect of ethyl acetate and acetone on the solution behavior of cellulose acetate butyrate (CAB) and carboxymehtylcellulose acetate butyrate (CMCAB) and on the characteristics of films obtained either by spin coating or adsorption was investigated. Viscosity and small angle X-ray scattering (SAXS) measurements showed that ethyl acetate is a better solvent than acetone for CAB e CMCAB. Films were characterized by means of ellipsometry, atomic force microscopy (AFM), sum frequency generation (SFG) and contact angle measurements. Spin-coated films of CMCAB from ethyl acetate solutions were thicker than those deposited from acetone solutions. AFM images revealed that CMCAB spin coated films from ethyl acetate solutions were homogeneous and flat. However, films obtained from solutions in acetone were very rough. SFG spectra showed that acetone binds strongly to SiO2/Si wafers, creating a new surface for CAB and CMCAB films. Surface energy values determined for spin-coated CAB and CMCAB were similar ~ (49,0 ± 0,5) mJ/m² with the dispersive component larger than the polar component. The adsorption of lysozyme, bovine serum albumin (BSA), concanavalin A and jacalin was more pronounced onto CMCAB films than that onto CAB films. Indicating that carboxymethyl group favored the adsorption process. The influence of surface roughness of CAB and CMCAB on protein adsorption has been investigated. In the case of CMCAB, protein adsorption was morepronounced onto rough films than that onto flat films. However, the roughness of CAB films exerted no significant influence on proteins adsorption
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-01-29
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.