Master's Dissertation
DOI
10.11606/D.46.2018.tde-26022018-145031
Document
Author
Full name
Tiago Luiz Ferreira
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2003
Supervisor
Committee
Bertotti, Mauro (President)
Mazo, Luiz Henrique
Torresi, Roberto Manuel
Title in Portuguese
Uso de métodos voltamétricos no estudo da deposição de óxidos de molibdênio em eletrodos de carbono vítreo e na investigação de propriedades estruturais em soluções micelares
Keywords in Portuguese
Eletroquímica
Molibdênio (Estudo)
Óxidos de molibdênio
Surfactantes
Tensoativo
Voltametria (Aplicações)
Abstract in Portuguese
A síntese de filmes inorgânicos mesoporosos por métodos eletroquímicos pode ser viabilizada com o uso de agregados de surfactantes, os quais atuam como moldes durante o processo de eletrodeposição. Neste contexto, são apresentados estudos sobre a obtenção de filmes de óxidos de molibdênio em superfícies de carbono vítreo por meio de deposição eletroquímica de Mo(VI) em meio ácido na presença de surfactantes apropriados. Desta maneira, estudos dos processos catalíticos referentes à redução de ânions oxigenados na superfície modificada na presença de surfactante são mostrados e comparados com os resultados oriundos de filmes depositados em solução sem o surfactante. Um breve estudo comparativo variando a concentração de Mo(VI) e o pH da solução geradora foi executado com a finalidade de verificar o efeito destes parâmetros sobre as características eletrocatalíticas do filme. Em duas condições experimentais especiais foram obtidos filmes de óxidos de molibdênio com cores distintas (azul escuro e amarelo). Experimentos espectroscópicos demonstram que a diferença na cor se deve à presença de espécies de Mo em diferentes estados de oxidação. Em virtude da existência de diferentes espécies de Mo(VI) em função da concentração do íon metálico e do pH e que, em conseqüência deste fato, filmes com características eletrocatalíticas distintas frente à redução catódica do iodato são produzidos, desenvolveu-se um método empregando microeletrodos para a quantificação de H+ em soluções concentradas de surfactante. A metodologia se baseia na prévia determinação do coeficiente de difusão do próton e medição da corrente limite em experimentos voltamétricos no meio contendo o surfactante. Neste trabalho também são mostrados estudos voltamétricos em soluções micelares de CTAB com o uso de sondas eletroativas com alta afinidade pelo interior micelar. Com a análise dos dados obtidos foi possível avaliar o coeficiente de difusão micelar (1.7 x 10-6 cm2/s) e o raio hidrodinâmico (13 Å) destes agregados em solução de KCI 0,05M. Estudos sobre a influência da concentração de surfactante e da natureza e concentração de eletrólito suporte no coeficiente de difusão dos agregados micelares foram realizados e constatou-se que existe mudança na estrutura das micelas em soluções contendo KCI em concentrações superiores a 0,20 M.
Title in English
The use of voltammetric methods in the study of the deposition of molybdenum oxides in vitreous carbon electrodes and the investigation of structural properties in micellar solution
Keywords in English
Electrochemistry
Molybdenum (Study)
Molybdenum oxides
Surfactants
Tensiatory
Voltammetry (Applications)
Abstract in English
In this work some studies involving the electrodeposition of molybdenum oxide thin films from solutions containing Mo(VI) are reported . The influence of the concentration of Mo(VI) and the pH on the characteristics of the obtained film were evaluated by spectroscopic techniques and by analysing the electrocatalytic effect of the modified electrode on the response for the cathodic reduction of iodate ions. Similar experiments were carried out at solutions containing surfactants such as Triton X-100 and Brij 56 as an attempt to generate mesoporous structures. However, no experimental evidence on the formation of such structures were obtained and the good response of the modified electrode prepared in surfactant medium was attributed to the formation of thin films which posses better performance towards the electrocatalytic reduction of iodate. Results were compared with those obtained f rom working solutions in the absence of surfactants. A methodology for acidity determination in solutions containing high concentrations of Triton X-100 was also developed. The procedure was based on the previous determination of the H+ diffusion coefficient in mixtures containing surfactant + water by using voltammetry with a platinum microelectrode. The results showed the influence of solution viscosity in the value of the diffusion coefficient of H+. Some results on the use of microelectrodes to measure the diffusion coefficient of ferrocene supported CTAB micelles were also performed. By using a classical theory that predicts the interaction between micelles as a function of the surfactant concentration, the diffusion coefficient of CTAB micelles at conditions of non-interaction (Dº) and the hydrodynamic radius (Rº) of the CTAB micelle at this experimental condition were found to be 1.7 x 10-6 cm2/s and 13 Å, respectively, at 0.05 M KCI solutions. The effect of different anions (bromide, chloride and fluoride) on the micellar diffusion coefficient was investigated and changes in the structure of spherical CTAB micelles at higher ionic strength values were postulated based on analysis of micellar interaction coefficient vs. CTAB concentration plots.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2018-02-26
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.