Tesis Doctoral
DOI
10.11606/T.46.1999.tde-26082014-154405
Documento
Autor
Nombre completo
Adélia Maria Lima da Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1999
Director
Tribunal
Matos, Jivaldo do Rosario (Presidente)
Fernandes Junior, Valter Jose
Luiz, Jose Marques
Machado, Luci Diva Brocardo
Vicentini, Geraldo
Título en portugués
Análise térmica aplicada à síntese e caraterização de óxidos mistos de níquel e terras raras
Palabras clave en portugués
Análise térmica
Caracterização
Compostos organometálicos
Lantanídios
Metal de transição
Método termoanalítico
Óxidos mistos
Química analítica
Síntese
Terras raras
Resumen en portugués
Este trabalho apresenta um estudo sistemático sobre síntese, caracterização e análise térmica aplicada a óxidos mistos dos tipos TR2NiO4 [TR = La, Eu e Y (III)] e TRNiO3 [TR = Pr, Nd e Sm (III)]. Os primeiros óxidos foram obtidos a partir da decomposição térmica de acetatos de terras raras e níquel utilizando-se três métodos distintos: (1) mistura mecânica; (2) evaporação do solvente e (3) cristalização com acetona. Os acetatos simples e binários foram caracterizados por análise elementar, espectroscopia de absorção na região do infravermelho, difração de raios X, TG/DTG, DSC e DTA. Os resultados revelaram a formação de sais binários quando utilizaram-se os métodos 2 e/ou 3. Os produtos da decomposição térmica foram basicamente os óxidos individuais e após tratamento térmico obteveram-se os óxidos desejados. Os óxidos TRNiO3 foram preparados através de três métodos diferentes: (1) mistura de óxidos; (2) precipitação simultânea de hidróxidos e (3) processo sol-gel. Estas amostras foram sinterizadas em temperaturas 650 ≤ T ≤ 1000°C e sob pressões de até 70 atm de O2, caracterizadas por difração de raios X, resistividade elétrica, microscopia eletrônica de varredura e calorimetria exploratória diferencial. Os resultados indicaram que o método sol-gel produziu óxidos monofásicos. Os outros dois métodos, mistura de óxidos e hidróxidos, produziram a fase desejada e traços dos óxidos individuais. Desta forma, concluiu-se que a escolha do método a ser utilizado é fundamental para a obtenção do óxido misto desejado.
Título en inglés
Thermal analysis applied to the synthesis and characterization of mixed oxides of nickel and rare earth
Palabras clave en inglés
Analytical chemistry
Characterization
Lanthanides
Mixed oxides
Organometallic compounds
Rare earth
Synthesis
Thermal Analysis
Thermoanalytical methods
Transition metal
Resumen en inglés
This work reports a systematic study on the synthesis, characterization and thermal analysis applied of mixed oxides type-TR2NiO4 [TR = La, Eu e Y (III)] e typeTRNiO3 [TR = Pr, Nd e Sm (III)]. The first oxides were prepared through thermal decomposition of rare earth and nickel acetates, which were synthesized by three methods: (1) mechanical mixture; (2) solvent evaporation and (3) crystallization with addition of acetone. The simply and binary acetates were characterized by elementare analyses, infrared spectroscopy, X ray diffraction, TG/DTG, DSC and DTA. The results revealed formation of binary salts when was used the second and/or third methods. The products of thermal decomposition were single oxides, but after thermal treatment were obtained the single phase of materials. The last oxides were prepared through three different methods: (1) mixture of oxides; (2) simultaneous precipitation of hydroxides and (3) sol-gel process. Samples were sintered at temperatures between 650 ≤ T ≤ 1000°C and under oxygen pressures until 70 atm, characterized by X ray diffraction, electrical resistivity, scanning electron microscopy and differential scanning calorimetry. The results revealed that the sol-gel method produced single phase oxides. The other two methods, mixture of oxides and hydroxides, led to have this phase with traces of single oxides. Therefore, it was concluded that the method used is fundamental to get the desired mixed oxides.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-08-26
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.