Disertación de Maestría
DOI
10.11606/D.46.2010.tde-13122010-101939
Documento
Autor
Nombre completo
Jones Leite Soares
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Vichi, Flavio Maron (Presidente)
Brito, Hermi Felinto de
Davolos, Marian Rosaly
Título en portugués
Síntese e caracterização de silicatos dopados com ións Cd2+ e Eu3+ pelo método do sal fundido com menor temperatura
Palabras clave en portugués
Características)
Química inorgânica
Sal Fundido
Silicato de Estrôncio
Silicatos (Síntese orgânica
Sol-Gel
Troca iônica (Métodos)
Resumen en portugués
Neste trabalho tivemos como objetivo sintetizar e caracterizar os ortossilicatos de elementos alcalino-terrosos com destaque para o Sr2SiO4, uma matriz hospedeira para íons dopantes como o cádmio II e o európio III, resultando em materiais com propriedades luminescentes. Outro objetivo é reduzir a temperatura de síntese pelos métodos aqui empregados em relação aos métodos convencionais descritos na literatura. Tanto a matriz quanto os sistemas dopados foram caracterizados por meio da difratometria de raios x, análise de área superficial e tamanho de poros, microscopia eletrônica de varredura e de transmissão. Os métodos empregados neste trabalho foram basicamente o da metátese e o do sal fundido, sendo que o método da metátese foi conduzido por sol-gel (utilizando-se sílica comercial e TEOS) e por precipitação em atmosfera ambiente e em atmosfera de nitrogênio. Já no método do sal fundido utilizamos duas temperaturas de síntese, 600 e 750ºC. A 750ºC foi utilizada uma mistura equimolar de cloreto de sódio e cloreto de potássio juntamente com nitrato de estrôncio e sílica mesoestruturada na proporção molar de 2:1. A 600ºC foi utilizada somente a mistura de nitrato de estrôncio e sílica mesoestruturada também na proporção molar de 2:1. Nestas duas formas de se conduzir a síntese por sal fundido utilizamos nitrato de sódio (proporção molar de Na/Si = 0,1) a fim de se facilitar a quebra das pontes de oxigênio da sílica e verificar a influência desse reagente sobre o produto final. Já o Ca2SiO4 e o Ba2SiO4 foram sintetizados apenas a 600ºC bem como as dopagens do Sr2SiO4 (1% em mol). Os resultados mostram uma densificação do produto em relação à sílica e a obtenção de nanofibras de silicatos obtidos pelo método do sal fundido. Já no método da metátese obtivemos carbonato de estrôncio e outros tipos de silicatos.
Título en inglés
Synthesis and Characterization of Silicates Doped with ions Cd2+ and Eu3+ by the Molten Salt Method by Lower Temperature
Palabras clave en inglés
Inorganic chemistry
Molten Salt
Sol-Gel
Strontium Silicate
Resumen en inglés
In this work our objective was to synthesize and characterize orthosilicates of alkaline-earth elements with emphasis on Sr2SiO4. This is a silicate host matrix for doping with ions such as cadmium II and europium III, resulting in materials with luminescent properties. Another objective is to reduce the synthesis temperature using the methods employed here when compared to conventional methods described the literature. Both the matrix and the doped systems were well characterized by X-ray diffraction, surface area and pore size distribution, scanning and transmission electron microscopy. The methods employed in this study were basically the metathesis and the molten salt; the metathesis method was conducted by sol-gel (using a commercial silica and tetraethyl orthosilicate TEOS) and precipitation in air and nitrogen atmospheres. In the molten salt method, two synthesis temperatures were used: 600 and 750ºC. At 750°C an equimolar mixture of sodium chloride and potassium chloride with strontium nitrate was used in addition to mesostructured silica in the molar ratio of 2:1. At 600°C only a mixture of strontium nitrate and mesostructured silica was used, also in the molar ratio of 2:1. In these two pathways, sodium nitrate (molar ratio Na/Si = 0.1) was used in order to facilitate the breakup of the silica oxygen bridges and its influence on the final product was also studied. Furthermore, Ca2SiO4 and Ba2SiO4 were synthesized only at 600ºC and the doping of Sr2SiO4 (1 mol %) was also carried out only at 600°C. The results show a densification of the product compared to the silica precursor and the formation of silicate nanofibers by the molten salt method. In the metathesis method we obtained strontium carbonate and other types of silicates.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-04-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.