Mémoire de Maîtrise
DOI
10.11606/D.46.2010.tde-13122010-101939
Document
Auteur
Nom complet
Jones Leite Soares
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2010
Directeur
Jury
Vichi, Flavio Maron (Président)
Brito, Hermi Felinto de
Davolos, Marian Rosaly
Titre en portugais
Síntese e caracterização de silicatos dopados com ións Cd2+ e Eu3+ pelo método do sal fundido com menor temperatura
Mots-clés en portugais
Características)
Química inorgânica
Sal Fundido
Silicato de Estrôncio
Silicatos (Síntese orgânica
Sol-Gel
Troca iônica (Métodos)
Resumé en portugais
Neste trabalho tivemos como objetivo sintetizar e caracterizar os ortossilicatos de elementos alcalino-terrosos com destaque para o Sr2SiO4, uma matriz hospedeira para íons dopantes como o cádmio II e o európio III, resultando em materiais com propriedades luminescentes. Outro objetivo é reduzir a temperatura de síntese pelos métodos aqui empregados em relação aos métodos convencionais descritos na literatura. Tanto a matriz quanto os sistemas dopados foram caracterizados por meio da difratometria de raios x, análise de área superficial e tamanho de poros, microscopia eletrônica de varredura e de transmissão. Os métodos empregados neste trabalho foram basicamente o da metátese e o do sal fundido, sendo que o método da metátese foi conduzido por sol-gel (utilizando-se sílica comercial e TEOS) e por precipitação em atmosfera ambiente e em atmosfera de nitrogênio. Já no método do sal fundido utilizamos duas temperaturas de síntese, 600 e 750ºC. A 750ºC foi utilizada uma mistura equimolar de cloreto de sódio e cloreto de potássio juntamente com nitrato de estrôncio e sílica mesoestruturada na proporção molar de 2:1. A 600ºC foi utilizada somente a mistura de nitrato de estrôncio e sílica mesoestruturada também na proporção molar de 2:1. Nestas duas formas de se conduzir a síntese por sal fundido utilizamos nitrato de sódio (proporção molar de Na/Si = 0,1) a fim de se facilitar a quebra das pontes de oxigênio da sílica e verificar a influência desse reagente sobre o produto final. Já o Ca2SiO4 e o Ba2SiO4 foram sintetizados apenas a 600ºC bem como as dopagens do Sr2SiO4 (1% em mol). Os resultados mostram uma densificação do produto em relação à sílica e a obtenção de nanofibras de silicatos obtidos pelo método do sal fundido. Já no método da metátese obtivemos carbonato de estrôncio e outros tipos de silicatos.
Titre en anglais
Synthesis and Characterization of Silicates Doped with ions Cd2+ and Eu3+ by the Molten Salt Method by Lower Temperature
Mots-clés en anglais
Inorganic chemistry
Molten Salt
Sol-Gel
Strontium Silicate
Resumé en anglais
In this work our objective was to synthesize and characterize orthosilicates of alkaline-earth elements with emphasis on Sr2SiO4. This is a silicate host matrix for doping with ions such as cadmium II and europium III, resulting in materials with luminescent properties. Another objective is to reduce the synthesis temperature using the methods employed here when compared to conventional methods described the literature. Both the matrix and the doped systems were well characterized by X-ray diffraction, surface area and pore size distribution, scanning and transmission electron microscopy. The methods employed in this study were basically the metathesis and the molten salt; the metathesis method was conducted by sol-gel (using a commercial silica and tetraethyl orthosilicate TEOS) and precipitation in air and nitrogen atmospheres. In the molten salt method, two synthesis temperatures were used: 600 and 750ºC. At 750°C an equimolar mixture of sodium chloride and potassium chloride with strontium nitrate was used in addition to mesostructured silica in the molar ratio of 2:1. At 600°C only a mixture of strontium nitrate and mesostructured silica was used, also in the molar ratio of 2:1. In these two pathways, sodium nitrate (molar ratio Na/Si = 0.1) was used in order to facilitate the breakup of the silica oxygen bridges and its influence on the final product was also studied. Furthermore, Ca2SiO4 and Ba2SiO4 were synthesized only at 600ºC and the doping of Sr2SiO4 (1 mol %) was also carried out only at 600°C. The results show a densification of the product compared to the silica precursor and the formation of silicate nanofibers by the molten salt method. In the metathesis method we obtained strontium carbonate and other types of silicates.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2011-04-04
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.