Disertación de Maestría
DOI
10.11606/D.46.2007.tde-18032008-114231
Documento
Autor
Nombre completo
Ruy Braz da Silva Filho
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Vichi, Flaáo Maron (Presidente)
Cosentino, Ivana Conte
Matos, Jivaldo do Rosário
Título en portugués
Estudo analítico de rotas de síntese de dióxido de titânio
Palabras clave en portugués
Automontagem
Combustão
Dióxido de titânio
Pechini
Sol-Gel
Resumen en portugués
Amostras de titânia foram sintetizadas por seis rotas diferentes: quatro pelo método sol-gel, utilizando condições e precursores distintos, por combustão de solução líquida e pelo método Pechini. Após tratamento térmico que variou de 100°C a 900°C, as amostras foram analisadas por difratometria de raios X, termogravimetria e pelo método BET de obtenção de áreas superficiais específicas. As amostras obtidas por sol-gel utilizando como precursores o isopropóxido de titânio (Pro) e o n-butóxido de titânio (But) geraram materiais de elevada área superficial, com alta fração molar de anatase e sem resíduos a 500°C. As amostras obtidas por sol-gel com excesso de íon peptizante (Nan) possuiam também altas áreas superficiais, além de estabilizarem a fase anatase a até 500°C, com resquícios de bruquita. As amostras obtidas por sol-gel utilizando um surfactante não iônico (Sur) demonstraram as maiores áreas superficiais, os menores tamanhos de cristais e estabilidade de anatase pura a 500°C. Esses materiais têm, pois, potencial para aplicação em fotocatálise, em células solares sensibilizadas por corantes e em células a combustível, entre outras. Os métodos da combustão (Com) e de Pechini (Pec) geraram produtos de baixa área superficial e com baixa ou com nenhuma fração de anatase. Porém, são métodos simples e eficientes de obtenção de titânia para aplicações que não necessitem da anatase como fase única.
Título en inglés
Study of synthetic routes for titanium dioxide
Palabras clave en inglés
Pechini
Self-assembly
Sol-gel
Solution combustion
Titanium dioxide
Resumen en inglés
Titania samples were prepared by six different routes, four of them by the sol-gel method using different precursors and reaction conditions, a solution combustion route and a Pechini method route. After thermal treatment ranging from 100 C to 900 C, the resulting materials were analyzed by X-ray diffraction, thermogravimetric analysis and surface area determination (BET method). The materials obtained by the sol-gel method using titanium isopropoxide (Pro) and titanium n-butoxide (But) as precursors yielded ceramics with high surface area, a high anatase molar fraction, without residues when heated at 500 C. Samples obtained by the sol-gel route using excess peptization agent (Nan) also showed high surface areas and yielded anatase with traces of brookite which was stable up to 500 C. Samples obtained using the sol-gel route with non-ionic surfactant (Sur) exhibit the highest surface area, smallest crystallite sizes and stable anatase with traces of brookite up to 500 C. These materials have, therefore, potential application in the areas of photocatalysis, dye- sensitized solar cells and fuel cells, among others. The combustion (Com) and Pechini (Pec) methods yielded materials with low surface area, with little or no presence of anatase. They are, however, simple and efficient methods for obtaining pure titania when the pure form of anatase is not a necessity.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-03-24
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.