Mémoire de Maîtrise
DOI
10.11606/D.46.2007.tde-18032008-114231
Document
Auteur
Nom complet
Ruy Braz da Silva Filho
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2007
Directeur
Jury
Vichi, Flaáo Maron (Président)
Cosentino, Ivana Conte
Matos, Jivaldo do Rosário
Titre en portugais
Estudo analítico de rotas de síntese de dióxido de titânio
Mots-clés en portugais
Automontagem
Combustão
Dióxido de titânio
Pechini
Sol-Gel
Resumé en portugais
Amostras de titânia foram sintetizadas por seis rotas diferentes: quatro pelo método sol-gel, utilizando condições e precursores distintos, por combustão de solução líquida e pelo método Pechini. Após tratamento térmico que variou de 100°C a 900°C, as amostras foram analisadas por difratometria de raios X, termogravimetria e pelo método BET de obtenção de áreas superficiais específicas. As amostras obtidas por sol-gel utilizando como precursores o isopropóxido de titânio (Pro) e o n-butóxido de titânio (But) geraram materiais de elevada área superficial, com alta fração molar de anatase e sem resíduos a 500°C. As amostras obtidas por sol-gel com excesso de íon peptizante (Nan) possuiam também altas áreas superficiais, além de estabilizarem a fase anatase a até 500°C, com resquícios de bruquita. As amostras obtidas por sol-gel utilizando um surfactante não iônico (Sur) demonstraram as maiores áreas superficiais, os menores tamanhos de cristais e estabilidade de anatase pura a 500°C. Esses materiais têm, pois, potencial para aplicação em fotocatálise, em células solares sensibilizadas por corantes e em células a combustível, entre outras. Os métodos da combustão (Com) e de Pechini (Pec) geraram produtos de baixa área superficial e com baixa ou com nenhuma fração de anatase. Porém, são métodos simples e eficientes de obtenção de titânia para aplicações que não necessitem da anatase como fase única.
Titre en anglais
Study of synthetic routes for titanium dioxide
Mots-clés en anglais
Pechini
Self-assembly
Sol-gel
Solution combustion
Titanium dioxide
Resumé en anglais
Titania samples were prepared by six different routes, four of them by the sol-gel method using different precursors and reaction conditions, a solution combustion route and a Pechini method route. After thermal treatment ranging from 100 C to 900 C, the resulting materials were analyzed by X-ray diffraction, thermogravimetric analysis and surface area determination (BET method). The materials obtained by the sol-gel method using titanium isopropoxide (Pro) and titanium n-butoxide (But) as precursors yielded ceramics with high surface area, a high anatase molar fraction, without residues when heated at 500 C. Samples obtained by the sol-gel route using excess peptization agent (Nan) also showed high surface areas and yielded anatase with traces of brookite which was stable up to 500 C. Samples obtained using the sol-gel route with non-ionic surfactant (Sur) exhibit the highest surface area, smallest crystallite sizes and stable anatase with traces of brookite up to 500 C. These materials have, therefore, potential application in the areas of photocatalysis, dye- sensitized solar cells and fuel cells, among others. The combustion (Com) and Pechini (Pec) methods yielded materials with low surface area, with little or no presence of anatase. They are, however, simple and efficient methods for obtaining pure titania when the pure form of anatase is not a necessity.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2008-03-24
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.