Disertación de Maestría
DOI
10.11606/D.46.2009.tde-26042010-133048
Documento
Autor
Nombre completo
Eiwalt Rodolfo Hanzl
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Vichi, Flávio Maron (Presidente)
Bizeto, Marcos Augusto
Matos, Jivaldo do Rosário
Título en portugués
Novas rotas de síntese de óxidos de titânio e mistos titânio-zircônio mesoestruturados via método sol-gel por template com surfactantes
Palabras clave en portugués
Atividade fotocatalítica
Mesoestruturas
Síntese sol-gel com template por surfactante
Titânia
Zircônia
Resumen en portugués
Uma nova rota de síntese via metodo sol-gel para óxido de titânio (titânia) e óxido misto titânio/zircônio (zircônia) é proposta neste trabalho. As amostras foram submetidas ao tratamento hidrotérmico e obteve-se compostos mesoestruturados e de elevada área superficial. Algumas amostras foram submetidas à calcinação a 450°C para a verificação da estabilidade a altas temperaturas. As amostras foram analisadas por difratometria de raios-x (DRX), espalhamento de raios-x de baixo ângulo (SAXS), área superficial através do método BET, por microscopia eletrônica de varredura por emissão de campo (FE-SEM), além de serem testadas na fotodegradação de corantes. Foram testados diferentes alcóxidos precursores, isopropóxido de titânio e n-butóxido de titânio; ácidos, clorídrico e nítrico; e surfactantes, Pluronic® P123, Brij® 700 e Brij® 98; e também variadas as quantidades de surfactantes utilizadas, para que fosse possível analisar como estas variações afetam a síntese dos compostos e se estabelecer uma nova rota padronizada utilizando-se os melhores precursores em quantidades ideais. Para efeito de comparação, foi testada uma rota alcalina de síntese, que levou ao material com área superficial mais elevada. Como resultado deste trabalho, foi desenvolvida uma nova rota de síntese para óxidos mesoestruturados de titânio e titânio/zircônio corn elevada área superficial, na qual a etapa de calcinação para remoção do surfactante foi eliminada. Algunas dos materiais preparados mostraram excelente desempenho na degradação fotocatalítica de um corante comercial.
Título en inglés
New synthetic routes for mesostructured titanium dioxide and mixed titanium-zirconium dioxide via surfactant-templated sol-gel methods
Palabras clave en inglés
Mesostructures
Photocalatytic activity
Surfactant template sol-gel synthesis
Titania
Zirconia
Resumen en inglés
A new sol-gel based synthetic route for titania and mixed titania-zirconia ceramic powders is proposed in this contribution. This route combines a surfactant-template strategy with hydrothermal treatment, yielding mesostructured compoundes with a high surface area. Some samples were calcined at 450 °C in order to verify the stability of the structures at these temperatures. The materials were characterized by x-ray diffraction (XRD), small angle x-ray scattering (SAXS), surface area (BET method), field emission scanning electron microscopy (FE-SEM), and were also tested in the photocatalytic degradation of selected dyes. Different precursor alcóxidos were used: titanium isopropoxide and titanium n-butoxide. Two different acids were used to catalyze the hydrolysis reaction, HCl and HNO3. Three surfactants were used as templating agents: Pluronic P123®, Brij 700®, and Brij 98®. The amount of surfactant was also changed in order to verify how these variations affect the surface area and morphology of the resulting compounds. For comparison, an alkaline route was also tested, in which the highest surface area was observed. As a result of this work, a new synthetic route for mesostructured titania and titania-zirconia mixed oxides was developed, in which the surfactant is removed without a calcinations step, resulting in compounds with high surface areas and, in some cases, excellent photocatalytic properties for the degradation of a dye.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-05-28
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.