Disertación de Maestría
DOI
10.11606/D.46.2004.tde-16052007-144206
Documento
Autor
Nombre completo
Romeu Casarano
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2004
Director
Tribunal
Petri, Denise Freitas Siqueira (Presidente)
El Seoud, Omar Abdel Moneim Abou
Gonçalves, Maria do Carmo
Título en portugués
Compósitos formados por polietileno modificado e celulose: obtenção e caracterização
Palabras clave en portugués
Alil glicidil éter
Celulose
Compósito
Polietileno
Polímeros
Processos químicos
Resumen en portugués
A primeira parte desta Tese incluiu a funcionalização em solução de polietileno linear de média densidade (LMDPE) com alil glicidil éter (AGE), na presença de peróxido de benzoíla (BPO) como iniciador de reações radicalares. A caracterização foi feita por espectroscopia no infravermelho com transformada de Fourier (FTIR) e o grau de funcionalização (GF) foi estimado por meio de duas curvas de calibração. Foi observado efeito do tipo de solvente sobre o GF. A segunda parte consistiu na funcionalização superficial por radiação ultravioleta (UV). Como monômeros foram usados AGE, anidrido maléico (MAH) e anidrido tetraidroftálico (THFAH). Como iniciadores, BPO e benzofenona (BP). A caracterização das superfícies foi realizada por medidas de ângulo de contato. THFAH apresentou a melhor performance. A terceira tratou da funcionalização por processamento reativo do LMDPE com AGE, na presença de BPO. A caracterização se deu por FTIR e o GF foi estimado conforme descrito acima. A funcionalização foi confirmada (indiretamente) por calorimetria diferencial exploratória, que evidenciou a diminuição do grau de cristalinidade com a funcionalização. Não foi possível confirmar a funcionalização por meio de análise elementar, termogravimetria e difração de raios X. A fragmentação das cadeias do LMDPE funcionalizado do ensaio 13 (e 13A) foi evidenciada por decréscimo no torque e nas propriedades mecânicas. Contudo, o índice de fluidez, surpreendentemente, diminuiu. Os valores relativamente superiores de resistência à tração e módulo de Young dos compósitos e blendas obtidos com LMDPE funcionalizado, contra os obtidos com LMDPE virgem, evidenciaram a interação favorável entre os grupos epóxidos inseridos nas cadeias do LMDPE e os grupos hidroxilas presentes no polissacarídeo. O aumento da adesão entre a matriz polimérica e as fibras de celulose foi confirmado por microscopia eletrônica de varredura e, qualitativamente, por quantidades relativamente maiores de resíduos remanescentes após extração em xileno sob refluxo.
Título en inglés
Composites made up of modified polyethyle and cellulose: obtainment and characterization
Palabras clave en inglés
Allyl glycidyl ether
Cellulose
Composites
Polyethylene
Polymers
Resumen en inglés
The first part of this work included the functionalization in solution of linear medium density polyethylene (LMDPE) with allyl glycidyl ether (AGE), in the presence of benzoyl peroxide (BPO) as free radical reaction initiator. The characterization was made by Fourier transform infrared spectroscopy (FTIR) and the degree of functionalization was estimated by means of two calibration curves. The type of solvent influenced the DF. The second part comprised the surface functionalization by ultraviolet (UV) radiation. AGE, maleic anhydride (MAH) and tetrahydrophthalic anhydride (THFAH) were used as monomers and BPO and benzophenone (BP) as initiators. Contact angle measurements were used to characterize the surfaces. THFAH showed the best performance. The third part dealt with the functionalization by reactive processing of LMDPE with AGE, in the presence of BPO. FTIR was used to characterize the samples and the degree of functionalization was estimated as described above. The functionalization was (indirectly) confirmed by differential scanning calorimetry. The degree of crystallinity decreased with the functionalization. The functionalization couldn?t be confirmed by elemental analysis, thermogravimetry and X-ray diffraction. The chain scissions of the chemical modified LMDPE of trial 13 (and 13A) were evidenced by reduction of torque and mechanical properties. However, the melt flow index diminished. The favorable interaction between epoxide groups inserted on LMDPE chains and hydroxyl groups present in polysaccharide caused the increase in tensile strength and Young?s modulus values for composites and blends in relation to those obtained with virgin LMDPE. The increase in adhesion between the polymeric matrix and cellulose fibers was also confirmed by scanning electron microscopy and, qualitatively, by relatively large amounts of remaining residues after extraction in refluxing xylene.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-05-05
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.