Thèse de Doctorat
DOI
https://doi.org/10.11606/T.46.2018.tde-20072018-180811
Document
Auteur
Nom complet
Paulo Cezar Frangiosa
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2002
Directeur
Jury
Catalani, Luiz Henrique (Président)
Kawano, Yoshio
Canevarolo Junior, Sebastião Vicente
Pardini, Vera Lucia
Wiebeck, Hélio
Titre en portugais
Produção de copolímeros de estireno com tempo de vida controlada
Mots-clés en portugais
Macromolécula
Photo-oxidation
Photodegradation
Plásticos
Polímeros
Polímeros (Química orgânica) (Produção)
Polistyrene
Química orgânica
Resumé en portugais
Este trabalho é direcionado ao estudo dos efeitos da radiação UV sobre amostras de poliestireno (PS) e de copolímeros de estireno com proporções variáveis de 2-trimetilsililóxi-1,3-butadieno (TSB, I), 2-metóxi-1,3-butadieno (MEB, II) e 2-etóxi-1,3-butadieno (ETB, III), em solução aerada, visando principalmente à amplificação da degradação ambiental do PS quando exposto a condições de intemperismo natural. (Ver no arquivo em PDF). Os polímeros foram sintetizados via polimerização radicalar em solução, resultando em uma massa molar ponderai média (Mw) de cerca de 30,0 kg/mol para o homo e copolímeros. Estes produtos, após serem submetidos a um processo de hidrólise na presença de fluoreto de tetrabutilamônio (série TSB) ou HCI aquoso (séries MEB e ETB), resultaram em PS contendo grupos carbonila na cadeia principal sendo, a seguir, isolados e caracterizados por meio de técnicas analíticas como espectroscopia de infravermelho (IR), análise elementar, cromatografia de exclusão por tamanho (SEC), espalhamento de luz estático dependente do tempo (TDSLS), análise térmica (TG e DSC) e microscopia eletrônica de varredura (MEV). As soluções poliméricas foram irradiadas com lâmpada de mercúrio de baixa pressão (99,5% de emissão a 254 nm), na presença de ar e à temperatura ambiente, por um período de dez horas. As alterações sofridas pelos polímeros foram acompanhadas por meio de medidas de IR, TDSLS e SEC. Os espectros no infravermelho mostraram um aumento contínuo da intensidade de algumas bandas: na região entre 3800 - 3000 cm-1, houve um alargamento das bandas que pode ser atribuído à formação de grupos hidroxila e/ou hidroperóxido; na região de 1900 - 1500 cm-1, observou-se o aparecimento de um ombro em 1712 cm-1, que pode ser atribuído à formação de grupos cetona e aldeído como funções terminais na cadeia do polímero e, na região entre 1500 - 1000 cm-1, o alargamento das bandas foi atribuído à formação de grupos anidrido. Os estudos realizados por TDSLS revelaram claramente que os copolímeros degradam com mais rapidez que o PS puro, e as taxas de degradação aumentam proporcionalmente ao aumento no teor de carbonilas incorporadas ao polímero. Tal observação tem suporte nas massas molares ponderais médias obtidas via SEC (Mw) dos fragmentos resultantes da fotólise, com valores cada vez menores com o aumento dos efeitos da fotodegradação, iniciando com cerca de 34,0 kg/mol (TSB5), por exemplo, e decrescendo a valores de Mw tão baixos quanto 4,8 kg/mol (TSB15). Para finalizar, tentou-se verificar o comportamento dos polímeros quando expostos a condições reais de utilização, submetendo-se corpos de prova a um envelhecimento acelerado em câmara de intemperismo artificial e avaliando seu comportamento mecânico. Os resultados mostraram que, para homo e copolímeros, houve uma redução na resistência à tração com o aumento do tempo de exposição (0 a 600 horas), sendo este efeito muito mais acentuado para os copolímeros.
Titre en anglais
Production of controlled-life styrene copolymers
Mots-clés en anglais
Macromolecule
Organic chemistry
Photo-oxidation
Photodegradation
Plastics
Polistyrene
Polymers
Polymers (Organic chemistry) (Production)
Resumé en anglais
This work was directed to the study of the UV radiation effects upon samples of polystyrene (PS) and copolymers of styrene with different fractions of 2-trimethylsililoxy-1,3-butadiene (TSB, I), 2-methoxy-1 ,3-butadiene (MEB, II) and 2-ethoxy-1,3-butadiene (ETB, III), in normally aerated solution, aiming at the optimization of the PS degradation when exposed to weathering conditions. (See in the PDF file). The polymers were prepared by free-radical polymerization in solution, resulting in average molecular weight (Mw) of about 30.0 kg/mol for the homo and copolymers. The resulting polymers were submitted to hydrolysis in the presence of tetrabutylamonium fluoride (TSB series) or aqueous HCI (MEB and ETB series), resulting in PS containing carbonyls inserted in its backbone. The polymers were isolated and characterized by infrared spectroscopy (IR), elemental analysis, size exclusion chromatography (SEC), time dependent static light scattering (TDSLS), thermal analysis (TG and DSC) and scanning electron microscopy (SEM). The polymeric solutions were irradiated with a low pressure mercury lamp (99.5% emission at 254 nm), in the presence of air at room temperature, for a period of 10 hours. The polymer changes were followed by IR, TDSLS and SEC. The infrared spectra showed a continuous increase in the intensity of some bands: the broad band in the region of 3800 - 3000 cm-1 was assigned to the formation of hydroxides or hydroperoxides groups; the band at 1900 - 1500 cm-1 with a shoulder at 1712 cm-1 can be assigned to ketones or aldehydes, which appear as chain termination groups and the band at 1500 - 1000 cm-1 was attributed to the formation of anhydrides. The TDSLS studies clearly showed that the copolymers degradated much faster than the pure PS, and the degradation rates were directly related to the increase in the TSB, MEB and ETB contents of the polymer. This observation is supported by the decreasing molecular weight values obtained by SEC (Mw) for the resulting fragments from photolysis, when the carbonylic content of the polymer increased, starting at around 34.0 kg/mol (TSB5), for instance, decreasing to Mw values as low as 4.8 kg/mol (TSB15). Finally, we tried to found out the polymer behavior when exposed to the real outdoor conditions of use, by submitting samples to an accelerated aging process in a Weather-o-Meter chamber and evaluating its mechanical behavior afterwards. The results showed that for both, homo and copolymers, there was a reduction in the tensile strength with increasing in the exposition time (0 to 600 hours). This behavior is much stronger in the copolymers.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2018-07-20
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.