Disertación de Maestría
DOI
10.11606/D.46.1999.tde-21122015-145356
Documento
Autor
Nombre completo
Guilherme Andrade Marson
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1999
Director
Tribunal
El Seoud, Omar A. (Presidente)
Curvelo, Antonio Aprigio da Silva
Quina, Frank Herbert
Título en portugués
Acilação de celulose em meio homogêneo
Palabras clave en portugués
Celulose
Éster
Polímeros (Química orgânica)
Química orgânica
Resumen en portugués
Um novo método de dissolução e acilação de celulose no sistema LiCl/N,N-dimetilacetamida (DMAC) foi desenvolvido e aplicado com sucesso nas seguintes celuloses: microcristalina (I), sisal (II), algodão(III) e bagaço de cana de açúcar (IV). O novo método tem as seguintes vantagens: a) uso de sistema acilante simples (anidridos alifáticos sem catalisadores); b) produção direta de ésteres simples (acetatos, propionatos e butiratos) e mistos (acetato/butirato), com eficiente controle do grau de esterificação; c) menor demanda de tempo e reagentes; d) desprezível degradação da celulose; e) eficiente recuperação/reciclagem do solvente e dos demais reagentes. Estudos por microscopia eletrônica de varredura revelam que em II e IV a penetração do solvente é mais lenta que em I devido à diferenças morfológicas. Constantes de velocidade e parâmetros de ativação do processo de descristalização de I e IV, foram determinados sob condições não isotérmicas, a partir do decaimento do índice de cristalinidade (determinado por espectroscopia no infravermelho). O processo de descristalização é globalmente endotérmico e aparentemente não depende do grau de polimerização (GP) da celulose de partida. A diferença na reatividade observada para as celuloses II a IV em relação a I, foi atribuída ao maior GP, maior flexibilidade da cadeia polimérica, além da agregação destas celuloses no sistema. O grau de acetilação individual das posições C6, C3 e C2 na unidade anidra de glicose, determinado por RMN de 13C, revela a seguinte ordem de reatividade para os grupos OH na UAG: C6 > C3 ≈ C2.
Título en inglés
Cellulose acylation in homogeneous
Palabras clave en inglés
Cellulose
Ester
Organic Chemistry
Polymer (Organic Chemistry)
Resumen en inglés
A novel procedure for cellulose dissolution and acylation in LiCl/ N,N-dimethylacetamide solvent system has been introduced and successfully applied to the following celluloses: microcrystalline (I), sisal (II), cotton (III) and sugar cane bagasse (IV). The novel procedure has the following attractive features: a) uses acid anhydride and requires no base catalyst; b) can be used for the direct preparation of esters and mixed esters; c) requires less amount of solvent and shorter time; d) causes negligible degradation of cellulose; e) permits recovery/recycling of DMAC and acid anhydride. Scanning electron microscopy studies show that swelling of celluloses II and IV by the solvent is slower than that of I, most probably due to morphological differences. Rate constants and activation parameters for decrystallization of I and IV have been determined from dependence of the index of crystallinity of cellulose, on time, under non-isothermal conditions. The decrystallization was found to be an endothermic process, negligibly dependent on the degree of polymerization (DP) of the starting cellulose. Differences in the reactivities between celluloses are related to GP, polymer chain flexibility and cellulose aggregation. The distribution of the acetyl moiety among the three OH groups was determined by 13C NMR, giving rise to the following order : C6 > C3 and C2.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-12-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.