Thèse de Doctorat
DOI
10.11606/T.46.2012.tde-02052013-141310
Document
Auteur
Nom complet
Tatiana Augusto
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2012
Directeur
Jury
Torresi, Susana Ines Cordoba de (Président)
Catalani, Luiz Henrique
Izumi, Celly Mieko Shinohara
Neves, Silmara das
Petri, Denise Freitas Siqueira
Titre en portugais
Síntese química de poli(3,4-etilenodioxitiofeno) (PEDOT): novas arquiteturas para diferentes aplicações
Mots-clés en portugais
Biocompatibilidade
Biodegradabilidade
Nanocompósito
Nanopartícula de ouro
Poli(lactídeo)
Resumé en portugais
Este trabalho apresenta estudos sobre a síntese química do PEDOT com o objetivo de desenvolver diferentes arquiteturas e propriedades para melhorar a taxa de degradabilidade deste polímero. As estratégias foram as preparações de uma blenda, um copolímero e um nanocompósito. O estudo foi iniciado pela síntese química oxidativa do PEDOT (poli (3,4- etilenodioxitiofeno)) em microestruturas utilizando condições brandas e ambientalmente amigáveis, porém o material obtido não apresentou solubilidade e boas condições de se produzir um filme. Então foi sintetizado quimicamente o PEDOT dopado com PSS (poli estireno sulfonado) (PEDOT:PSS), o mesmo foi usado para preparar blendas com o PLGA (poli (ácido láctico-co-glicólico), para melhorar sua degradabilidade. Foi possível produzir um filme fino e nanoestruturado através de deposição eletrostática camada por camada (LBL) que pode ser utilizado para modificação de eletrodos ou de suportes tridimensionais para engenharia celular. Para garantir a degradabilidade do material, foi realizada a síntese de copolímeros de PEDOT e PLLA (poli(lactídeo)) em que foi variada a proporção de PEDOT na cadeia polimérica. Os copolímeros foram caracterizados por IV, RMN, UV, análises térmicas e submetidos a testes de degradabilidade e de viabilidade celular, apresentando excelentes resultados. Foi possível a obtenção de microfibras deste material. A outra alternativa estudada foi a síntese de um nanocompósito, preparado através da síntese química do PEDOT, partindo do monômero EDOT (3,4- etilenodioxitiofeno)usando HAuCl4 como oxidante e NaPSS como dopante e dispersante. O nanocompósito obtido foi caracterizado apresentando diâmetros médio próximos de 4 nm e com uma estrutura caroço-casca, apresentando nanopartícula de ouro como caroço e o polímero PEDOT:PSS como casca. Foram obtidos filmes deste material por deposição por evaporação de solvente, LBL, utilizando como policátion o PDDA (cloreto de poli (dialil dimetil amônio)) e quitosana, e por deposição eletroforética, que apresentou excelentes propriedades eletrocrômicas como rápidos tempos de respostas com bons contrastes ópticos
Titre en anglais
Chemical synthesis of poly(3,4-ethylenedioxythiophene) (PEDOT): new archictetures for different aplications
Mots-clés en anglais
Biocompatibility
Biodegradability
Gold nanoparticle
Nanocomposite
Poly(lactide)
Resumé en anglais
This work presents studies about the chemical synthesis of PEDOT (Poly(3,4-ethylenedioxythiophene)) with the aim of preparing different architectures and properties to improvement the degradability rate of this polymer. The strategies used to achieve this pupose were the preparation of polymer blends, copolymers and nanocomposites. The study was started by the chemical synthesis of microstructures PEDOT in mild and environment friendly conditions, but the material did not show solubility which enable film formation. Then, PEDOT was synthetized by chemical synthesis doped with PSS (poly(styrene sulfonic acid)), (PEDOT:PSS) to prepare blends with PLGA (poly(lactic-co-glycolic acid)) to improve its degradability. It was possible to prepare a thin and nanostructured film, by electrostatic layer-by-layer deposition (LBL), which could be used for electrodes or scaffold surface modification. In order to ensure the material's degradability, PEDOT and PLLA (poly(lactide)) copolymers were prepared, changing PEDOT proportion in the polymeric structure. The copolymers were characterized by, IR, NMR, UV, thermal analysis and then degradability and cell viability tests, which shown important results. Fibers were able to be obtained with these materials. The next strategy was the preparation of a nanocomposite by one-spot chemical synthesis, initiated by the monomer EDOT (3,4- ethylenedioxythiophene) using HAuCl4 as oxidant and NaPSS as both dopant and dispersant. The nanocomposite obtained was characterized showing diameter of around 4nm and a core-shell structure, with gold nanoparticle as core and PEDOT:PSS as the shell. Films were obtained by this material by casting, by LBL, using PDDA (Poly(diallyldimethylammonium) chloride) and chitosan as polycations, and by electrophoretic deposition. The latter method shows excellent characteristics as fast response time with a good optical contrast
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2013-08-23
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.