Disertación de Maestría
DOI
https://doi.org/10.11606/D.46.2017.tde-20092017-110015
Documento
Autor
Nombre completo
William Wakim
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2017
Director
Tribunal
Matos, Jivaldo do Rosario (Presidente)
Kawano, Yoshio
Machado, Luci Diva Brocardo
Título en portugués
Estudo do fosqueamento de tintas em pó, sistema poliéster/TGIC
Palabras clave en portugués
Análise térmica
Cura em estufa
Fosqueamento
Poliéster
Resina
TGIC
Tinta em pó
Resumen en portugués
O presente trabalho propôs-se a estudar o fenômeno de fosqueamento em filmes de tinta em pó feitos a partir de resinas poliésteres sólidas pelo sistema conhecido como Triglicidilisocianutato (TGIC). Este fenômeno é indesejado e ocorre na ocasião de mistura de lotes de tintas produzidos independentemente com resinas poliésteres sólidas que compartilham as mesmas fórmulas, especificações e processo industrial. Amostras de uma tríade de resinas poliéster, que apresenta uma particular relação de fosqueamento, foram estudadas por termogravimetria/ termogravimetria derivada (TG/DTG), calorimetria exploratória diferencial (DSC), espectroscopia de ressonância magnética nuclear de Hidrogênio (1H-RMN), cromatografia de permeação em gel (GPC), análise térmica diferencial (DTA) e espectroscopia de infravermelho com transformada de Fourier (FTIR). A partir da análise minuciosa dos resultados obtidos em cada técnica escolhida, não se notou diferenças significativas que pudessem vir a justificar o fosqueamento indesejado para os lotes estudados. Estas avaliações nos permitiram concluir que o fenômeno não ocorre por contaminação industrial dos materiais e que alguma relação latente de fosqueamento por blenda seca deve ainda ser revelada por estudo subsequente.
Título en inglés
Matting study for powder coatings, polyester/TGIC system
Palabras clave en inglés
Matting
Oven cure
Polyester
Powder coating
Resin
TGIC
Thermal analysis
Resumen en inglés
The present work endeavored to study the matting phenomenon of powder coatings films made of solid polyester resins through a system known as Triglycidyl isocyanurate (TGIC). This phenomenon is an undesired result and occurs when at the time of blending paint batches produced independently with polyester resins that share the same formula, specifications e industrial process. Samples of a polyester resin triad, that shared a particular matting relation, were studied by thermogravimetry/ thermogravimetry derivative (TG/DTG), differential scanning calorimetry nuclear magnetic resonance (1H-NMR), gel permeation chromatog r(aDpShCy), proton (GPC), differential thermal analysis (DTA) and Fourier transform infrared spectroscopy (FTIR). Through in-depth analyses of all results obtained from each chosen method, no accountable differences, that could justify the undesired matting phenomenon, were noticed. These evaluations paved us the way to conclude that the studied phenomenon was not occurring due to industrial contamination, and that some latent dry blend matting relation is still to be revealed by an ensuing study.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-09-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.