Tesis Doctoral
DOI
10.11606/T.54.1982.tde-22042014-160005
Documento
Autor
Nombre completo
Jose Alberto Rodrigues Jordao
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1982
Director
Tribunal
Souza, Milton Ferreira de (Presidente)
Aegerter, Michel Andre
Camargo, Paulo Cesar de
Morato, Spero Penha
Panepucci, Horacio Carlos
Título en portugués
Estudo de defeitos elásticos em sólidos: ultra-som e relaxação dielétrica
Palabras clave en portugués
Defeitos elásticos
Relaxação dielétrica
Ultra-som
Resumen en portugués
Este trabalho trata de estudos realizados sobre o comportamento das fronteiras dos domínios magnéticos em mono-cristais de (Mn - Zn) Fe2 03 como também das propriedades elásticas de defeitos puntuais em mono-cristais de NaCl: NaF: M++ . Foram aplicadas técnicas do oscilador composto de Marx com controlador automático de velocidade e atenuação ultrassônica, a técnica do pulso-eco ultrassônico e corrente termo-estimulada (I.T.C.) com pressão uniaxial. Para os cristais de NaCl: NaF: M++ , determinamos a simetria e os parâmetros de relaxação que provocam os picos de ITC chamados de B e C. Foi mostrado que o pico C é devido a relaxação de uma vacância entre as posições nn em torno do eixo que passa pelos íons F- M++ , enquanto o pico B é uma relaxação envolvendo uma transição da vacância entre as posições nn e nnn. Para as ferrites as fronteiras dos domínios magnéticos comportam-se elasticamente como dislocações, mostrando uma atenuação ultrassônica que á dependente da amplitude do campo elástico
Título en inglés
Study of elastic defects in solids: ultrasound and dielectric relaxation
Palabras clave en inglés
Dielectric relaxation
Elastic defects
Ultrasound
Resumen en inglés
This work is concerned with the behavior of magnetic domain walls of (Mn - Zn) Fe2O3 single crystals, as well as, with elastic properties of point defects in NaCl: NaF: M++ single crystals. The measurements were carried out using the following experimental techniques: pulse-echo, ITC under uniaxial stress and composite oscillator of the Marx type with automatic control of velocity. For the NaCl: NaF: M ++ crystals the symmetry of the defect that gives rise to ITC peaks B and C was determined, as well as its relaxation parameters. It was shown that peak C is due to vacancy relaxation between nn positions around the axis M++F- ions while peak B is a relaxation involving between the nn and nnn vacancy positions. For the ferrites the magnetic domain walls behave elastically as dislocations therefore having an ultrassonic attenuation that is amplitude dependent on the elastic field
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-06-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.