Tese de Doutorado
DOI
10.11606/T.54.1982.tde-22042014-160005
Documento
Autor
Nome completo
Jose Alberto Rodrigues Jordao
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1982
Orientador
Banca examinadora
Souza, Milton Ferreira de (Presidente)
Aegerter, Michel Andre
Camargo, Paulo Cesar de
Morato, Spero Penha
Panepucci, Horacio Carlos
Título em português
Estudo de defeitos elásticos em sólidos: ultra-som e relaxação dielétrica
Palavras-chave em português
Defeitos elásticos
Relaxação dielétrica
Ultra-som
Resumo em português
Este trabalho trata de estudos realizados sobre o comportamento das fronteiras dos domínios magnéticos em mono-cristais de (Mn - Zn) Fe2 03 como também das propriedades elásticas de defeitos puntuais em mono-cristais de NaCl: NaF: M++ . Foram aplicadas técnicas do oscilador composto de Marx com controlador automático de velocidade e atenuação ultrassônica, a técnica do pulso-eco ultrassônico e corrente termo-estimulada (I.T.C.) com pressão uniaxial. Para os cristais de NaCl: NaF: M++ , determinamos a simetria e os parâmetros de relaxação que provocam os picos de ITC chamados de B e C. Foi mostrado que o pico C é devido a relaxação de uma vacância entre as posições nn em torno do eixo que passa pelos íons F- M++ , enquanto o pico B é uma relaxação envolvendo uma transição da vacância entre as posições nn e nnn. Para as ferrites as fronteiras dos domínios magnéticos comportam-se elasticamente como dislocações, mostrando uma atenuação ultrassônica que á dependente da amplitude do campo elástico
Título em inglês
Study of elastic defects in solids: ultrasound and dielectric relaxation
Palavras-chave em inglês
Dielectric relaxation
Elastic defects
Ultrasound
Resumo em inglês
This work is concerned with the behavior of magnetic domain walls of (Mn - Zn) Fe2O3 single crystals, as well as, with elastic properties of point defects in NaCl: NaF: M++ single crystals. The measurements were carried out using the following experimental techniques: pulse-echo, ITC under uniaxial stress and composite oscillator of the Marx type with automatic control of velocity. For the NaCl: NaF: M ++ crystals the symmetry of the defect that gives rise to ITC peaks B and C was determined, as well as its relaxation parameters. It was shown that peak C is due to vacancy relaxation between nn positions around the axis M++F- ions while peak B is a relaxation involving between the nn and nnn vacancy positions. For the ferrites the magnetic domain walls behave elastically as dislocations therefore having an ultrassonic attenuation that is amplitude dependent on the elastic field
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2014-06-12
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.