Disertación de Maestría
DOI
10.11606/D.54.1991.tde-02042015-115744
Documento
Autor
Nombre completo
Doroteia de Fatima Bozano
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1991
Director
Tribunal
Aegerter, Michel Andre (Presidente)
Ionashiro, Massao
Souza, Dulcina Maria Pinatti Ferreira de
Título en portugués
Preparação e caracterização de cerâmica tipo mulita (3Al2O3-2SiO2) pelo processo sol-gel
Palabras clave en portugués
Não disponível
Resumen en portugués
Apresenta-se um método alternativo de preparação de cerâmica mulita (3Al2O3-2SiO2) pelo processo sol-gel. Os sóis são preparados a partir de uma mistura de isopropanol, alcóxido de alumínio (sec-butóxido de alumínio), alcóxido de silício (TEOS) e acetilacetona. A água para reação de hidróliseé obtida da umidade ambiente (método de hidrólise lenta). A influência da quantidade de solvente e da área de contato sol/atmosfera sobre as características do gel obtido foram estudadas através das técnicas BET e espectroscopia de infravermelho. Os géis calcinados analisados por microssonda EDX são homogêneos quimicamente, eles cristalizam em temperaturas tão baixas quanto 980°C. As temperaturas típicas de eliminação de hidroxilasve compostos orgânicos as transformações de fase e as respectivas perdas de massa durante as diversas transformações sofridas pelo gel obtido foram determinadas por técnicas de ATD e TG. A evolução das fases cristalográficas em função dos tratamentos térmicos foi estudada por técnicas de difração de raio-X e espectroscopia de infravermelho. Foi observado que a 980°C ocorre a formação de uma mistura de fase mulita/Al-Si spinel que se transforma em mulita ortorrômbica a temperaturas superiores a 1250°C. Um diâmetro médio de 280 nm foi obtido após a moagem do gel calcinado a 500°C. As amostras obtidas através de prensagem uniaxial ou isostática e posteriormente tratadas a 1550°C apresentam baixa densidade que foi relacionada com a pequena quantidade de água utilizada na reação de hidrólise do sol percursor. Apresenta-se também um estudo do comportamento da área superficial BET de géis do sistema sílica/alumina obtidos por diversos métodos de preparação e precursores
Título en inglés
Not available
Palabras clave en inglés
Not available
Resumen en inglés
A new method to prepare mulite ceramic (3Al2O3-2SiO2) by sol-gel process is presented. Sols are prepared from isopropanol aluminum alcoxide (aluminum sec-butoxide), silicium alcoxide (TEOS) and acetylacetone mixture the water for hydrolysis reaction is gotten from ambient moisture (slow hydrolysis method). The influence f solvent concentration and the sol/atmosphere contact area on the gel characteristics was investigated by BET and infrared spectroscopy techniques. The calcined gels are chemically homogeneous under EDX microssonde analysis; they crystallize at so low temperature as 980°C. The typical temperatures of hydroxyl and organic compound elimination, phase transformation and respective mass losses slong the various transformation attained by gel were determined by DAT and TGA techniques. The crystallographic phases evolution under heat treatment was investigated by x-ray diffraction and infrared spectroscopy. It was observed at 980°C occur the formation of a mixture mullite/Al-Si spinel phase that transform into orthorhombic mullite at temperatures greater than 1250°C. An average diameter of 280nm was obtained after 500°C calcined gel ball milling. The samples obtained by uniaxial or isostatic pressing and the treated at 1550°C presented low density that was related to low amount of water used in the hydrolysis reaction of precursor sol. A research on the behavior of BET superficial area of gels of silica/alumina gels obtained by different methods of preparation and precursor is also reported
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
DoroteiaBozanoM.pdf (7.57 Mbytes)
Fecha de Publicación
2015-04-06
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.