Disertación de Maestría
DOI
10.11606/D.54.1983.tde-07042010-143424
Documento
Autor
Nombre completo
João Mariz Guimarães Neto
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1983
Director
Tribunal
Giacometti, José Alberto (Presidente)
Oliveira, Luiz Nunes de
Wagner, Jerome
Título en portugués
Descargas termo-estimuladas no teflon fep-a em circuito aberto.
Palabras clave en portugués
Corrente termo estimulada
Descarga corona
Teflon fep-A
Resumen en portugués
Foram construídas duas montagens experimentais: Com a primeira, mediu-se o decaimento do potencial de superfície em circuito aberto, em função da temperatura; com a segunda mediu-se diretamente a corrente termo-estimulada (derivada do potencial de superfície em circuito aberto) aquecendo-se a amostra a uma taxa constante. Usando essas técnicas estudamos as propriedades de transporte e armazenamento de cargas no Teflon FEP-A, carregado com corona. Usando a segunda técnica, verificou-se que amostras descarregadas, do citado material, podem liberar portadores de cargas positivas que dão origem a uma corrente anômala, que pode interferir nas medidas de corrente termo-estimulada de amostras carregadas positivamente. Estudou-se o comportamento das curvas de corrente em amostras com e sem tratamento térmico, carregadas com corona tanto positiva como negativa. Além disto, é feita uma discussão dos resultados por nós obtidos e os publicados na literatura.
Título en inglés
Open-circuit TSD method in Teflon fep-A
Palabras clave en inglés
Corona discharge
Teflon fep-A
TSD
Resumen en inglés
Two experimental systems were constructed: with the first the surface potential could be measured, while with the second, its derivative with respect to the time (the so called open circuit current). In both cases the measurements were performed while heating previously positive or negative corona charged FEP-A Teflon 25μm samples. The results gave information about charge storage and transport properties in this material. During the work it was noticed that positive ions maybe emitted from Teflon surface. This unexpected phenomenon was followed in some detail in order to know how far it influences the usual currents. This study led us to carry measurements in previously annealed samples, whose behavior was found to differ from that of virgin samples. Our results were compared with those found in the literature.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-06-28
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.