• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
Documento
Autor
Nombre completo
Mauro Miguel Costa
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1991
Director
Tribunal
Giacometti, José Alberto (Presidente)
Alfaro, Renê Armando Moreno
Eiras, José Antonio
Título en portugués
Estudo do comportamento elétrico de filmes de PVDF na fase alfa
Palabras clave en portugués
Corrente constante
Polímeros ferroelétricos
PVDF
Triodo de corona
Resumen en portugués
A técnica do triodo de corona com corrente constante foi utilizada para carregar amostras de PVDF na fase α, acompanhando a evolução do potencial de superfície durante o carregamento. Com essa técnica foi possível não só obter a fase αp a partir da fase α como também analisar o comportamento elétrico de ambas as fases. Os resultados obtidos em ambiente úmido mostram que a forma geral das curvas de potencial nas amostras carregadas com corona positiva e negativa são similares, ou seja, no início do carregamento tem-se um salto inicial, continua crescendo numa taxa mais lenta até alcançar um valor máximo de potencial e a partir deste valor decai para um regime estacionário. Os valores de potenciais alcançados na superfície da amostra não foram suficientes para gerar campos elétricos da ordem 1.5MV/cm, requeridos para induzir uma transição para a fase αp. Apesar de ocorrerem mudanças no comportamento elétrico durante os carregamentos, nenhuma mudança na estrutura das amostras foi detectada, usando a técnica de difratometria de raios-X. Em ambiente seco foi verificado que, durante o carregamento, o potencial na superfície da amostra alcançava valores altos quando comparado aos obtidos em ambiente úmido. Verificou-se também, que as amostras apresentavam enrugamento, característicos de materiais poliméricos. As mudanças ocorridas devido ao carregamento foram detectadas pela técnica de raios-X, confirmando a mudança de estrutura para αp. O comportamento ferroelétrico das amostras na fase αp, foi identificado pela curva de evolução do potencial de superfície, onde se avalia a quantidade de polarização ferroelétrica adquirida. As mudanças de estrutura e das propriedades elétricas em ambiente seco foram irreversíveis.
Título en inglés
Electric behavior of alfa phase PVDF films
Palabras clave en inglés
Constant current
Corona triode
Ferroelectric polymers
PVDF
Resumen en inglés
The constant current corona triode was used for charging α-PVDF samples and monitoring their surface potential buildup during poling. It is shown that the method allows one to obtain the polar αp form of PVDF from the non-polar α-form and also to analuse electrical characteristics of both forms. The experimental results obtained with samples under humid conditions show a similar behavior for positive and negative corona. There is na initial steep increase in the surface potential which then increases passing through a maximum value, and decreases until a steady state is reached. The maximum values attained are not sufficiently high to attain electric fields of around 1.5MV/cm required for causing a phase change from α to αp. Furthermore, no change in the structure of the samples is noted in X-ray diffractograms. For measurments carried out under dry conditions, on the other hand, the sample surface potential attain much higher values. The samples become wrinkled after being submitted to these high electric fields (> 1.5MV/cm), and this is characteristic of ferroelectric materials. The change to αp from samples is confirmed by the structural changes exhibited in X-ray diffractograms. The ferroelectric behavior of the αp samples is further identified by the surface potential buildup, from which the remanent polarization can be inferred. The structural as well as the electric changes caused by the corona charging are found to be irreversible.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
MauroMiguelCostaM.pdf (3.01 Mbytes)
Fecha de Publicación
2014-04-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.