Tesis Doctoral
DOI
10.11606/T.54.1992.tde-09042014-144141
Documento
Autor
Nombre completo
Neri Alves
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1992
Director
Tribunal
Giacometti, José Alberto (Presidente)
Faria, Roberto Mendonça
Kawano, Yoshio
Oliva, Glaucius
Varela, Jose Arana
Título en portugués
Estudo da polarização ferroelétrica no copolímero P (VDF/TrFE)
Palabras clave en portugués
Corrente constante
P(VDF-TrFE)
Polarização ferroelétrica
Resumen en portugués
Usando-se a técnica do triodo de corona com corrente constante estudaram-se as propriedades ferroelétricas dos copolímeros P(VDF-TrFE) contendo diferentes teores de VDF. Descrevem-se as metodologias usadas na preparação de amostras por solução, a caracterização por raios X e DSC e a determinação do grau de cristalinidade. Apresentam-se o princípio de funcionamento da técnica do triodo de corona com corrente constante e a equivalência das curvas de potencial de superfície com as curvas de histerese. Mostra-se que a condução elétrica pode ser desprezada quando as medidas são realizadas em atmosfera com baixo valor de umidade. O valor do campo coercivo e da polarização remanente foram determinados a partir das curvas de subida do potencial de superfície, sendo o valor da polarização diretamente proporcional ao grau de cristalinidade das amostras. Esses resultados foram analisados supondo-se que os filmes de P(VDF-TrFE) podem ter duas fases cristalinas. Também são discutidos os modelos teóricos usados para interpretar as curvas de subida do potencial de superfície.
Título en inglés
Study of ferroelectric polarization in P(VDF/TrFE) copolymer
Palabras clave en inglés
Constant current
Ferroelectric polarization
P(VDF-TrFE)
Resumen en inglés
Ferroelectric properties of P(VDF-TrFE) copolymers having different contents of VDF were investigated using the corona triode with constant current. The casting procedure for the sample preparation, the characterization by X rays and DSC, and the determination of the degree of crystalinity were presented. The corona triode method allowing to charge samples with a Constant current and the equivalence between the potential buildup curves and hysteresis curves are presented. The coercive field and the remanent polarization were determined from the potential buildup curves and it was found that the polarization is linearly dependent on the degree of crystalinity. Results were discussed taking into account two different crystaline phases which could exists in P(VDF-TrFE). Also, it was presented theoretical models aiming to fit the potential buildup curves.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
NeriAlvesD.pdf (4.66 Mbytes)
Fecha de Publicación
2014-04-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.