Tese de Doutorado
DOI
10.11606/T.54.1992.tde-09042014-144141
Documento
Autor
Nome completo
Neri Alves
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1992
Orientador
Banca examinadora
Giacometti, José Alberto (Presidente)
Faria, Roberto Mendonça
Kawano, Yoshio
Oliva, Glaucius
Varela, Jose Arana
Título em português
Estudo da polarização ferroelétrica no copolímero P (VDF/TrFE)
Palavras-chave em português
Corrente constante
P(VDF-TrFE)
Polarização ferroelétrica
Resumo em português
Usando-se a técnica do triodo de corona com corrente constante estudaram-se as propriedades ferroelétricas dos copolímeros P(VDF-TrFE) contendo diferentes teores de VDF. Descrevem-se as metodologias usadas na preparação de amostras por solução, a caracterização por raios X e DSC e a determinação do grau de cristalinidade. Apresentam-se o princípio de funcionamento da técnica do triodo de corona com corrente constante e a equivalência das curvas de potencial de superfície com as curvas de histerese. Mostra-se que a condução elétrica pode ser desprezada quando as medidas são realizadas em atmosfera com baixo valor de umidade. O valor do campo coercivo e da polarização remanente foram determinados a partir das curvas de subida do potencial de superfície, sendo o valor da polarização diretamente proporcional ao grau de cristalinidade das amostras. Esses resultados foram analisados supondo-se que os filmes de P(VDF-TrFE) podem ter duas fases cristalinas. Também são discutidos os modelos teóricos usados para interpretar as curvas de subida do potencial de superfície.
Título em inglês
Study of ferroelectric polarization in P(VDF/TrFE) copolymer
Palavras-chave em inglês
Constant current
Ferroelectric polarization
P(VDF-TrFE)
Resumo em inglês
Ferroelectric properties of P(VDF-TrFE) copolymers having different contents of VDF were investigated using the corona triode with constant current. The casting procedure for the sample preparation, the characterization by X rays and DSC, and the determination of the degree of crystalinity were presented. The corona triode method allowing to charge samples with a Constant current and the equivalence between the potential buildup curves and hysteresis curves are presented. The coercive field and the remanent polarization were determined from the potential buildup curves and it was found that the polarization is linearly dependent on the degree of crystalinity. Results were discussed taking into account two different crystaline phases which could exists in P(VDF-TrFE). Also, it was presented theoretical models aiming to fit the potential buildup curves.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
NeriAlvesD.pdf (4.66 Mbytes)
Data de Publicação
2014-04-11
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.