Disertación de Maestría
DOI
10.11606/D.54.1983.tde-09122013-113235
Documento
Autor
Nombre completo
Hermes Adolfo de Aquino
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1983
Director
Tribunal
Ferreira, Guilherme Fontes Leal (Presidente)
Gross, Bernhard
Gupta, Hari Mohan
Título en portugués
Experiências de polarização e condução nos polímeros PVDF e FEP
Palabras clave en portugués
Condução e polarização
Polímeros PVDF e FEP
Resumen en portugués
Nesta dissertação relatamos os resultados de medidas elétricas realizadas, a maioria delas, em folhas de 25μm de polivinilidene de flúor (PVDF), e em menor número em folhas de tetrafluoretileno-hexafluorpropileno (Teflon FEP). Correntes de polarização sob variadas tensões e de despolarização foram medidas a várias temperaturas e com temperatura variável. O PVDF sofre modificações, possivelmente estruturais, sob aquecimento acima de 100°C quando um campo elétrico parece produzir uma limpeza elétrica, resultando uma condutividade menor. As polarizações são do tipo t-n, indicando, no caso do PVDF uma distribuição em freqüências e para o FEP tratado termicamente a 200°C, uma em energia. Apesar das amostras de PVDF fornecerem resultados pouco reprodutíveis, pode-se concluir que para os campos empregados o comportamento é razoavelmente linear na polarização e superlinear para a condutividade. Observou-se também um comportamento anômalo da corrente, no PVDF, sob a ação prolongada de campo aplicado, mesmo para as menores tensões. Para o FEP o comportamento da corrente para os diversos campos usados foi bastante irregular embora as polarizações e as subseqüentes despolarizações coincidissem na maioria dos casos
Título en inglés
Experiments on conduction and polarization in PVDF and FEP polymers
Palabras clave en inglés
Conduction and polarization
PVDF and FEP polymers
Resumen en inglés
We present here the results of electrical measurements performed, most of them, in 25μm foils of polyvinylidene fluoride (PVDF), and fewer in flois of tetrafluorethilene-hexafluorpropilene (Teflon FEP). Polarization currents under varied applied voltages and the corresponding depolarizations were measured at constante temperature and during heating and cooling. The PVDF exhibits modifications, possibly its structure changes, if heated above 100°C; in this case an electric field seems to clean the sample since its conductivity strongly decreases thereafter. The polarizations are of the t-n type, poiting to a distribution of frequencies inPVDF and of energies in FEP previously annealed at 200&#C. Although the results are poorly reproducible, some conclusions could be drawn for the PVDF: the polarization is nearly linear with the field but the conductivity shows a super linear dependence. An anomalous behavior of the current was observed at long time under tension, even the smallest use here. In the case of FEP, the magnitude of the current in relation with the voltage hás shown an irregular behavior, although polarization and the corresponding depolarization do indeed coincide in most cases
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-12-10
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.