Dissertação de Mestrado
DOI
10.11606/D.54.1983.tde-09122013-113235
Documento
Autor
Nome completo
Hermes Adolfo de Aquino
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1983
Orientador
Banca examinadora
Ferreira, Guilherme Fontes Leal (Presidente)
Gross, Bernhard
Gupta, Hari Mohan
Título em português
Experiências de polarização e condução nos polímeros PVDF e FEP
Palavras-chave em português
Condução e polarização
Polímeros PVDF e FEP
Resumo em português
Nesta dissertação relatamos os resultados de medidas elétricas realizadas, a maioria delas, em folhas de 25μm de polivinilidene de flúor (PVDF), e em menor número em folhas de tetrafluoretileno-hexafluorpropileno (Teflon FEP). Correntes de polarização sob variadas tensões e de despolarização foram medidas a várias temperaturas e com temperatura variável. O PVDF sofre modificações, possivelmente estruturais, sob aquecimento acima de 100°C quando um campo elétrico parece produzir uma limpeza elétrica, resultando uma condutividade menor. As polarizações são do tipo t-n, indicando, no caso do PVDF uma distribuição em freqüências e para o FEP tratado termicamente a 200°C, uma em energia. Apesar das amostras de PVDF fornecerem resultados pouco reprodutíveis, pode-se concluir que para os campos empregados o comportamento é razoavelmente linear na polarização e superlinear para a condutividade. Observou-se também um comportamento anômalo da corrente, no PVDF, sob a ação prolongada de campo aplicado, mesmo para as menores tensões. Para o FEP o comportamento da corrente para os diversos campos usados foi bastante irregular embora as polarizações e as subseqüentes despolarizações coincidissem na maioria dos casos
Título em inglês
Experiments on conduction and polarization in PVDF and FEP polymers
Palavras-chave em inglês
Conduction and polarization
PVDF and FEP polymers
Resumo em inglês
We present here the results of electrical measurements performed, most of them, in 25μm foils of polyvinylidene fluoride (PVDF), and fewer in flois of tetrafluorethilene-hexafluorpropilene (Teflon FEP). Polarization currents under varied applied voltages and the corresponding depolarizations were measured at constante temperature and during heating and cooling. The PVDF exhibits modifications, possibly its structure changes, if heated above 100°C; in this case an electric field seems to clean the sample since its conductivity strongly decreases thereafter. The polarizations are of the t-n type, poiting to a distribution of frequencies inPVDF and of energies in FEP previously annealed at 200&#C. Although the results are poorly reproducible, some conclusions could be drawn for the PVDF: the polarization is nearly linear with the field but the conductivity shows a super linear dependence. An anomalous behavior of the current was observed at long time under tension, even the smallest use here. In the case of FEP, the magnitude of the current in relation with the voltage hás shown an irregular behavior, although polarization and the corresponding depolarization do indeed coincide in most cases
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2013-12-10
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.