Disertación de Maestría
DOI
10.11606/D.54.1978.tde-10042015-105656
Documento
Autor
Nombre completo
Carlos Tres Suchicital Ayala
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1978
Director
Tribunal
Zimmerman, Robert Lee (Presidente)
Qualifik, Paul
Terrile, Maria Cristina
Título en portugués
Efeito piezoelétrico induzido em polímeros sintéticos
Palabras clave en portugués
Não disponível
Resumen en portugués
Construiu-se um aparelho para medir os componentes real e imaginário da constante piezelétrica de tensão d = d’ id”, para filmes poliméricos, com um campo elétrico d.c. externo constante. A razão da constante piezelétrica e o campo elétrico constante é equivalente a (ε + κ)s, onde ε é a constante dielétrica, κ é a constante de eletro-estrição, e s é a constante elástica de compliance . A dependência na temperatura, da piezoeletricidade induzida pelo campo, da uma informação das propriedades elétricas e elásticas dos polímeros. Depois de aquecer um filme de Poli (Cloreto de Vinila) até aproximadamente 95°C, seguido de um resfriamento à temperatura ambiental, mantendo um campo elétrico externo d.c. constante, observa-se a piezoeletricidade em um campo elétrico d.c. nulo, o qual sugere a introdução de uma polarização residual no filme
Título en inglés
Not available
Palabras clave en inglés
Not available
Resumen en inglés
An apparatus is devised for measuring the real and imaginary components of the piezoelectric stress constant d = d’ id” for polymer films with a d.c. bias field. Electric field induced piezoelectricity is observed for films of several types of polymer. The ratio of the piezoelectric constant to the d.c. bias field gives (ε + κ)s, where ε is the dielectric constant, κ is the electrostriction constant, and s is the elastic compliance constant. The temperature dependence of the field induced piezoelectricity gives, therefore, combined information of dielectric and elastic properties of polymers. After heating to about 95°C followed by cooling to roam temperature, maintaining a constant d.c. bias on a poly (vinyl chloride) film, piezoelectricity is observed at null d.c. field, which suggests the introduction of a residual polarization in the film
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-04-10
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.