Disertación de Maestría
DOI
10.11606/D.54.1993.tde-12092007-172500
Documento
Autor
Nombre completo
André Mauricio Brinatti
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1993
Director
Tribunal
Mascarenhas, Yvonne Primerano (Presidente)
Santos, Carlos de Oliveira Paiva
Torriani, Iris C Linares de
Título en portugués
Análise por cristalografia de raios X de uma liga de Heusler (Co2ScSn) e de material biocerâmico através do Método de Rietveld.
Palabras clave en portugués
Cristalografia
Difração de raios X
Liga de Heusler
Material biocerâmico
Métodos de Rietveld.
Resumen en portugués
Foram analisados, por difração de raios X, dois materiais policristalinos: uma liga de Heusler (C02ScSn), onde amostras originárias da mesma preparação foram submetidas a vários tratamentos térmicos distintos, e um material biocerâmico. Para o refinamento utilizou-se o Método de Rietveld. Na análise feita com a liga de Heusler (C02ScSn) tornou-se evidente uma segunda fase: C02Sn, e que não foi refinada por não haver um modelo de estrutura para a mesma. Assim, o refinamento foi efetuado, apenas para a estrutura conhecida, escolhendo algumas alternativas de função perfil, tais como as funções Gaussiana, pseudo-Voigt e Thompson¬-Cox-Hastings pseudo-Voigt modificada. A radiação de fundo também foi refinada utilizando o polinômio de quinta ordem. Os resultados obtidos foram equivalentes. Dos resultados obtidos nos refinamentos, conclui-se que as condições de preparação das amostras Fl17 (proveniente da amostra original, tratada a 600°C por 60 horas, em seguida moída, tratada a 200°C por 80 horas e submetida a resfriamento lento) e Al17 (proveniente da amostra original, tratada a 800°C por 48 horas e submetida a resfriamento lento), foram as mais satisfatórias. As amostras Fl17 e Al17 foram mais satisfatórias, respectivamente, segundo os índices de discordância do refinamento: qualidade do refinamento, de perfil e de perfil ponderado, e segundo os índices de discordância do refinamento: de Bragg e de fator de estrutura. Pela análise feita com o material biocerâmico tornou-se evidente a presença de duas fases cristalinas: hidroxiapatita [Ca10 (PO4) 6 (OH)2] e whitlockite [βCa3(PO4)2], e com o refinamento foi possível calcular a composição da mistura nas amostras. Pode-se concluir que o processo utilizado na obtenção da amostra HAIII103 ([Jarcho, M., Bolen, H. C., Thomas, M. B., Bobick, J., Kay, J. F. and Doremus, R. H., 1976. J. Matter. Sci., 11, 2027-2035], e homogeneizada com a mistura de colágeno: polímeros hidrofílicos) mostrou-se mais adequado, já que a mesma apresentou-se mais rica em hidroxiapatita.
Título en inglés
X-Ray crystallography analysis of a heusler alloy (Co2ScSn) and bioceramic material by Rietveld method
Palabras clave en inglés
Bioceramic material
Crystallografhy
Heusler alloy
Rietveld method
X-Ray diffraction
Resumen en inglés
Two polycrystalline materials were analysed by X-ray diffraction: a Heusler alloy (Co2ScSn), where samples originating from the same preparation were submitted to several different thermal treatments, and a bioceramic material. The Rietveld method was employed for the refinement. The analysis of the Heusler alloy clearly revealed the presence of a second phase: CO2Sn, which was not refined due to the absence of a structural model. Thus, the refinement was performed, only for the component with known structural model, choosing several alternative profile functions such as Gaussian, pseudo-Voigt and Thompson-Cox-Hastings modified pseudo-Voigt. The background radiation also was refined using a fifth order polynomial. The results obtained were equivalent. From the results obtained by the refinement it can be concluded that the preparation conditions of sample Fl17 (arising from the original sample treated at 600OC for 60 hours, ground, treated at 200OC for 80 hours and annealed) and Al17 (arising from the original sample treated at 800OC for 48 hours and annealed) were more satisfactory. The samples F117 and Al17 were more satisfactory, respectivelly, according to the disagreement factors goodness of fit, pattern and weighted pattern, and according to the disagreement factors Bragg and structure factor. The analysis of the bioceramic material clearly revealed the presence of two crystalline phases: hydroxyapatite [Ca10(PO4)6(OH)2] and whitlockite [β-Ca3(PO4)2] and via the refinement it was possible to calculate its composition. The procedure used to obtain sample HAIII103 ([Jarcho, M., Bolen, H. C., Thomas, M. B., Bobick, J., Kay, J. F. and Doremus, R. H., 1976. J. Matter. Sci., 11, 2027-2035], and homogeneized with a mixture of collagenous: hidrophylic polymers) proved to be the most adequate since this sample was richer in hydroxyapatite.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
AndreBrinatti.pdf (4.11 Mbytes)
Fecha de Publicación
2007-09-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.