Mémoire de Maîtrise
DOI
10.11606/D.54.1991.tde-13022015-145954
Document
Auteur
Nom complet
Braz Bello Júnior
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1991
Directeur
Jury
Campos, Milton Soares de (Président)
Mergulhão, Sérgio
Rodrigues, Edson
Titre en portugais
Síntese, dopagem, propriedades elétricas e caracterização do poli-(para-fenileno) (PPP)
Mots-clés en portugais
Não disponível
Resumé en portugais
O poli- (para-fenileno) (ppp) foi obtido na forma de pó, utilizando-se um processo de preparação química onde o benzeno foi polimerizado na presença de cloreto de Alumínio e cloreto de cobre. Amostras sólidas na forma de discos, com diâmetro da ordem de 1.25cm e espessuras variáveis entre 0.4 e 1mm foram obtidas pela compactação do pó à uma pressão de 2.28x105N/m2. Para medidas elétricas foram depositados, por evaporação no vácuo, contatos de alumínio nas duas faces das amostars. O ppp na forma de pó, foi dopado com diferentes concentrações de cloreto de ferro dissolvido em nitrometano. Para a caracterização das amostras dopadas e não dopadas foram utilizadas técnicas de medida da condutividade elétrica em função do campo elétrico e da temperatura, medidas do espectro de infravermelho, difração de raios-x, espalhamento de raios-x à baixo angulo e ressonância paramagnética eletrônica. A análise da condutividade em função da temperatura, mostrou que o processo de condução pode ser explicado por um modelo de hopping desenvolvido para semicondutores amorfos. Por difração de raios-x foi possível calcular os parâmetros de cada cela unitária. Por espalhamento de raios-x a baixo angulo, caracterizar as superfícies como fractais por medidas da intensidade do feixe espalhado em função do vetor de espalhamento. Por ressonância magnética nuclear de alta resolução, foi possível observar como o ferro entra na cadeia do polímero, como também verificar uma possível aplicação do modelo de solitons ao PPP
Titre en anglais
Not available
Mots-clés en anglais
Not available
Resumé en anglais
Poly-(p-phenylene) (PPP) was obtained in powder form, using a chemical processes where benzene was polimerizated by treatment with aluminum chloride-cupric chloride. The solid samples in disc form, with diameter of 1.25cm and thickness between 0.4 and 1 mm, has been obtained by powder compactation with pression of 2.28 N/m2. For electrical measurements, vacuum deposition of aluminum eletrodes in the two sides of the samples were used. PPP in powder form was doped with different concentrations of the iron chloride dissolved in dry nitronethane. Measurements of the electrical condutivity as a function of the electric field and temperature, infrared absorption, x-ray diffraction, small angle x-ray diffraction and electron paramagnetic resonance were made. Analysis of the electrical conductivity as a function of temperature showed that the conduction processes could be explained by a hopping model developed for amorphous semiconductors. Using x-ray diffraction was possible to calculate the unit cell parameters. For the small angle x-ray scattering was possible to characterize the surface of the polymer as a fractal using the intensities of the scattered beam as a function of the scattering vector. With high resolution nuclear magnetic resonance technique has been possible to observe not only how the iron atoms enter in the polymer chain but also to show one application of the soliton model for PPP.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
BrazBelloJuniorM.pdf (4.73 Mbytes)
Date de Publication
2015-02-19
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.