Disertación de Maestría
DOI
10.11606/D.54.1985.tde-13022015-155857
Documento
Autor
Nombre completo
Fernando Josepetti Fonseca
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1985
Director
Tribunal
Campos, Milton Soares de (Presidente)
Alvarez, Fernando
Castro Neto, Jarbas Caiado de
Título en portugués
Desenvolvimento de uma célula solar de silício para aplicações espaciais
Palabras clave en portugués
Não disponível
Resumen en portugués
Este trabalho teve como objetivo o desenvolvimento de um conjunto de processos para a fabricação de células solares de silício para utilização espacial, do tipo convencional. As células solares de silício monocristalino desenvolvidas neste trabalho possuem junção rasa, obtida por difusão de fósforo em substrato tipo-p (com resistividade de 1 ou 10 Ohm.cm), grades de contato de Ti/Pd/Ag e camada antirefletora de dióxido de titânio. Em células de 4cm2 foram obtidas eficiências de conversão de até 13,6% com fator de preenchimento de 0,77 em substratos de 1 Ohm.cm e 13% e 0,76 em substratos de 10 Ohm.cm. Células construídas com substratos de 10 Ohm.cm apresentaram melhor tolerância à danos de radiação que as de 1 Ohm.cm. São analisadas as influências da camada antirefletora, resistividade de substrato, geometria e técnicas de deposição da grade de contatos no desempenho elétrico das células
Título en inglés
Not available
Palabras clave en inglés
Not available
Resumen en inglés
The objective of this work was the study and the development of techniques for the fabrication of silicon solar cells, of conventional type, for space applications. The single-crystal silicon solar cells were fabricated on p-type substrates of 1 and 10 Ohm.cm resistivities by thermal diffusion of phosphorus from liquid source. The anti-reflective coatings were made from titanium dioxide obtained by reactive sputtering of a titanium target. A triple titanium-palladium-silver layer was utilized to prepare the contacts. Conversion efficiencies of up to 13.6% and fill factors of 0.77 were obtained in cells fabricated on 1 Ohm.cm substrates and efficiencies of 13% and fill factor of 0.76 were obtained in cells fabricated in 10 Ohm.cm substrates. Better radiation damage tolerance was observed in cells with 10 Ohm.cm substrates when compared with 1 Ohm.cm substrate cells. The inf1uences of the anti-reflective coatings, substrate resistivities, and contact grid geometry and grid deposition techniques on cell performance are analyzed
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-02-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.