Disertación de Maestría
DOI
10.11606/D.54.1987.tde-13122013-165105
Documento
Autor
Nombre completo
Edinilton Morais Cavalcante
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1987
Director
Tribunal
Andreeta, Jose Pedro (Presidente)
Jordao, Jose Alberto Rodrigues
Nascimento, Otaciro Rangel
Título en portugués
Preparação, caracterização e propriedades elétricas de monocristais de hexafluoreto de fósforo e potássio: KPF6
Palabras clave en portugués
Composto KPF6
Monocristal
Propriedades elétricas
Resumen en portugués
Realizamos crescimento de monocristal de Hexafluoreto de Fósforo e Potássio:KPF6 pelo método de crescimento em solução aquosa e o estudo das propriedades elétricas. Para isso foram feitas medidas, de solubilidade, tempo de incubação, espectroscopia dispersiva no infra-vermelho, difração de raios-X, condutividade elétrica e constante dielétrica no intervalo de temperatura de hélio líquido a 300°C. Foram detectadas três transições de fases estruturais em APROXIMADAMENTE 0°C, -14,4°C e 193°C e impurezas de CO-23, responsável pelo aumento da condutividade elétrica na região extrínsica. Na defermação do grupo PF6 durante a transição de fase estrutural em -14,4°C há surgimento de um dipolo elétrico com valor de 12,2x10-18ues.cm. E observamos o congelamento do grupo PF6 por volta de -41&#C
Título en inglés
Preparation, characterization and electrical properties of single crystals of hexafluoride phosphorus and potassium: KPF6
Palabras clave en inglés
Electrical properties
KPF6 compound
Single crystal
Resumen en inglés
It was made the growth of a Potassium Hexafluophosphate: KPF6 monocrystal method of growth in aqueous solution and the study of its electrical properties. With this purpose, it was use of solubility, incubation time, dispersive espectroscopy on the infrared region, X-ray diffraction, electrical conductivity and dieletrical Constant in the range of temperature between liquid helium and 573K. It was detected three strutural phase transitions in 273K, 258,6K and 80K and impurities like CO-23. In the deformation of the PF6 group, during the structural phase transition in 258,6K, electrical dipole appears with a value 12,2.10-18ues.cm. It was observed the freezing of PF6 group near 232K
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-12-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.