Dissertação de Mestrado
DOI
10.11606/D.54.1987.tde-13122013-165105
Documento
Autor
Nome completo
Edinilton Morais Cavalcante
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1987
Orientador
Banca examinadora
Andreeta, Jose Pedro (Presidente)
Jordao, Jose Alberto Rodrigues
Nascimento, Otaciro Rangel
Título em português
Preparação, caracterização e propriedades elétricas de monocristais de hexafluoreto de fósforo e potássio: KPF6
Palavras-chave em português
Composto KPF6
Monocristal
Propriedades elétricas
Resumo em português
Realizamos crescimento de monocristal de Hexafluoreto de Fósforo e Potássio:KPF6 pelo método de crescimento em solução aquosa e o estudo das propriedades elétricas. Para isso foram feitas medidas, de solubilidade, tempo de incubação, espectroscopia dispersiva no infra-vermelho, difração de raios-X, condutividade elétrica e constante dielétrica no intervalo de temperatura de hélio líquido a 300°C. Foram detectadas três transições de fases estruturais em APROXIMADAMENTE 0°C, -14,4°C e 193°C e impurezas de CO-23, responsável pelo aumento da condutividade elétrica na região extrínsica. Na defermação do grupo PF6 durante a transição de fase estrutural em -14,4°C há surgimento de um dipolo elétrico com valor de 12,2x10-18ues.cm. E observamos o congelamento do grupo PF6 por volta de -41&#C
Título em inglês
Preparation, characterization and electrical properties of single crystals of hexafluoride phosphorus and potassium: KPF6
Palavras-chave em inglês
Electrical properties
KPF6 compound
Single crystal
Resumo em inglês
It was made the growth of a Potassium Hexafluophosphate: KPF6 monocrystal method of growth in aqueous solution and the study of its electrical properties. With this purpose, it was use of solubility, incubation time, dispersive espectroscopy on the infrared region, X-ray diffraction, electrical conductivity and dieletrical Constant in the range of temperature between liquid helium and 573K. It was detected three strutural phase transitions in 273K, 258,6K and 80K and impurities like CO-23. In the deformation of the PF6 group, during the structural phase transition in 258,6K, electrical dipole appears with a value 12,2.10-18ues.cm. It was observed the freezing of PF6 group near 232K
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2013-12-18
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.