Tesis Doctoral
DOI
10.11606/T.54.1984.tde-14102009-112032
Documento
Autor
Nombre completo
Roberto Mendonça Faria
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1984
Director
Título en portugués
Medidas de absorção dielétrica e condutividade induzida por radiação ionizante em polifluoreto de vinilideno
Palabras clave en portugués
Absorção dielétrica
Armadilhamento
Condutividade induzida
Radiação ionizante
Resumen en portugués
Neste trabalho reportamos numerosas medidas de correntes devido á condutividade induzida por raios-x, durante e após a irradiação em amostras de filme de PVF2. Uma série de paramêtros de medidas foram variados, tais como: o campo elétrico, a taxa de radiação, o tipo de eletrodo, as condições atmosféricas das medidas e a espessura das atmosferas. Foram também feitas medidas de correntes de cargas e descarga de Absorção Dielétrica em ar úmido, em ar seco, em argônio e no vácuo. Curvas de correntes termo-estimuladas em amostras irradiadas e não-irradiadas permitiram verificar a presença de armadilhas no material, e também obter parâmetros dessas armadilhas. Finalmente desenvolveu-se modelo teórico e calculou-se curvas características para as correntes induzidas que concordaram com as curvas experimentais. O ajuste das curvas permitiu a determinação de valores numéricos para parâmetros de material.
Título en inglés
Dielectric abosrption and induced conductivity by ionizing radiation in PVDF
Palabras clave en inglés
Dielectric absorption
Induced conductivity
Ionization radiation
Trapping-detrapping
Resumen en inglés
We measured the radiation induced conductivity (RIC), prompt and delayed, in PVDF films under varied conditions, such as: electric fields, dose rate, electrode material, atmospheric environment and sample thickness. Polarization and depolarization absorption currents were also measured in dry and wet air, in argon and vacuum. Thermostimulated current measurements were carried out in irradiate samples showing that excited charges maybe captured by traps. Analysis of these currents led to the evaluation of the trap parameters. A model was developed in order interpret the transient RIC, assuming trapping, detrapping, recombination centers and also taking into account the extraction time.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-12-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.