Tesis Doctoral
DOI
10.11606/T.54.1986.tde-16032015-103214
Documento
Autor
Nombre completo
Choyu Otani
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1986
Director
Tribunal
Aegerter, Michel Andre
Craievich, Aldo Felix
Luengo, Carlos Alberto
Mascarenhas, Yvonne Primerano
Torriani, Iris C Linares de
Título en portugués
Variações estruturais e de propriedades físicas do coque de lignina
Palabras clave en portugués
Não disponível
Resumen en portugués
A lignina, subproduto da obtenção de álcool a partir da madeira, foi analisada quimicamente, verificando-se que contém aproximadamente 35% em peso de carbono fixo e um baixo teor de cinzas (0,70% em peso). Este material foi tratado termicamente a diferentes temperaturas, entre 300 e 2600°C, sob atmosfera inerte, obtendo-se coques com estrutura, composição química e propriedades físicas variadas. A caracterização estrutural dos coques de lignina tratados a diferentes temperaturas foi efetuada por meio da técnica de difração de raio-X, de espalhamento de raio-X a baixo engulo e de espectrofotometria de absorção ótica na região do infravermelho. A correlação da caracterização estrutural com a composição química e com as características físicas, dos coques obtidos, permitiu formalizar um modelo estrutural da transformação deste material em escalas a nível atômico e "macroscópico". Os resultados obtidos das caracterizações possibilitaram indicar as temperaturas adequadas dos tratamentos térmicos, a serem escolhidas, conforme as exigências da aplicação do coque a ser obtido
Título en inglés
Not available
Palabras clave en inglés
Not available
Resumen en inglés
The studied lignin is a by-product of the process of ethanol production from eucaliptus. It was heat-treated under inert atmosphere conditions at increasing temperatures from 300°C up to 2600°C. This material has about 35 weight % of carbon yield and low ash content (0.70 w %). The structural variations were studied by wide-angle X-ray diffraction, small-angle X-ray scattering and infra-red spectroscopy. The bulk and the "real" density of the samples have also been determined as a function of the heat treatment temperatures. These experimental results enabled us to establish a mechanism of structure variation based on the formation of a graphite-like and porous structure within the initially amorphous lignin matrix. It has been possible to specify the adequate heat treatment temperature based upon the lignin coke applications
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
ChoyuOtaniD.pdf (13.50 Mbytes)
Fecha de Publicación
2015-03-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.