Thèse de Doctorat
DOI
10.11606/T.54.1986.tde-16032015-103214
Document
Auteur
Nom complet
Choyu Otani
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1986
Directeur
Jury
Aegerter, Michel Andre
Craievich, Aldo Felix
Luengo, Carlos Alberto
Mascarenhas, Yvonne Primerano
Torriani, Iris C Linares de
Titre en portugais
Variações estruturais e de propriedades físicas do coque de lignina
Mots-clés en portugais
Não disponível
Resumé en portugais
A lignina, subproduto da obtenção de álcool a partir da madeira, foi analisada quimicamente, verificando-se que contém aproximadamente 35% em peso de carbono fixo e um baixo teor de cinzas (0,70% em peso). Este material foi tratado termicamente a diferentes temperaturas, entre 300 e 2600°C, sob atmosfera inerte, obtendo-se coques com estrutura, composição química e propriedades físicas variadas. A caracterização estrutural dos coques de lignina tratados a diferentes temperaturas foi efetuada por meio da técnica de difração de raio-X, de espalhamento de raio-X a baixo engulo e de espectrofotometria de absorção ótica na região do infravermelho. A correlação da caracterização estrutural com a composição química e com as características físicas, dos coques obtidos, permitiu formalizar um modelo estrutural da transformação deste material em escalas a nível atômico e "macroscópico". Os resultados obtidos das caracterizações possibilitaram indicar as temperaturas adequadas dos tratamentos térmicos, a serem escolhidas, conforme as exigências da aplicação do coque a ser obtido
Titre en anglais
Not available
Mots-clés en anglais
Not available
Resumé en anglais
The studied lignin is a by-product of the process of ethanol production from eucaliptus. It was heat-treated under inert atmosphere conditions at increasing temperatures from 300°C up to 2600°C. This material has about 35 weight % of carbon yield and low ash content (0.70 w %). The structural variations were studied by wide-angle X-ray diffraction, small-angle X-ray scattering and infra-red spectroscopy. The bulk and the "real" density of the samples have also been determined as a function of the heat treatment temperatures. These experimental results enabled us to establish a mechanism of structure variation based on the formation of a graphite-like and porous structure within the initially amorphous lignin matrix. It has been possible to specify the adequate heat treatment temperature based upon the lignin coke applications
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
ChoyuOtaniD.pdf (13.50 Mbytes)
Date de Publication
2015-03-16
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.