Disertación de Maestría
DOI
10.11606/D.54.1980.tde-16092010-191916
Documento
Autor
Nombre completo
José de Anchieta Rodrigues
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1980
Director
Título en portugués
Propriedades de tração do Nb policristalino dopado com hidrogênio
Palabras clave en portugués
Dutilidade
Encruamento
Hidrogênio
Niobio
Propriedades mecânicas
Resistência mecânica
Soluto intersticial
Taxa de deformação
Tração
Resumen en portugués
Foi estudado, através de ensaio de tração, o Nb policristalino com teor de hidrogênio de 0 a 50 partes por milhão em peso (ppm-p) nas temperaturas de 223, 273 e 293 K. Os ensaios de tração a velocidades constantes foram realizados com taxas iniciais de deformaçao de 4,2 X 10-5 e 42 X 10-5 s-1 , e os parâmetros de ductilidade e resistência mecânica foram analisados em função da concentração de hidrogênio. Foram também obtidos o coeficiente de sensitividade a taxa de deformação (m) e o volume de ativação (V) através de ensaios de tração, alternando-se abruptamente a taxa de deformação entre os valores acima mencionados, em sucessivos pontos da curva tensão-deformação. Para o cálculo destes dois últimos parâmetros foi proposta uma análise detalhada, considerando-se os efeitos elásticos e o encruamento durante a deformação plástica uniforme. Todo o estudo foi acompanhado por análise fratográfica Que permitiu verificar três comportamentos de ruptura da liga Nb-H, dependendo do teor de hidrogênio e da temperatura. A 223K foi observado que há uma forte redução de ductilidade do Nb para teores de hidrogênio até 10 ppm-p, sendo que para este teor o seu comportamento foi totalmente frágil
Título en inglés
Tensile properties of polycristalline Nb dopped with hydrogen
Palabras clave en inglés
Ductility
Hydrogen
Interstitial solute
Mechanical properties
Mechanical strenght
Niobium
Strain rate
Tensile
Work hardening
Resumen en inglés
Tensile testing at 223, 273 and 293 K was carried out on polycrystalline Nb dopped from 0 to 50 parts per million in weight (ppm-wt) of Hydrogen. The tensile testing at constant velocity was done at 4,2 X 10 -5 and 42 X 10-5 s-1 of initial strain rate, and the ductility and strength parameters was analysed as a function of the hydrogen content. It was also obtained the strain rate sensitivity (m) and the activation volume (V), from tensile testing, cycling between the two above specified strain rates, at several points of the stress-strain curve. For the calculation of this two last parameters it was proposed a detailed analysis, considering the elastic effect and the work hardening during the uniform plastic deformation. All these studies was followed by fratographic analysis that alowed the identification of three rupture behavior for the Nb-H alloy, depending of the temperature and the hydrogen content. At 223 K, it was observed that there is a strong embrittlement of Nb for hydrogen content up to 10 ppm-wt, and for this value the behavior was completely brittle
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-09-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.