Tesis Doctoral
DOI
10.11606/T.54.1992.tde-16102014-173028
Documento
Autor
Nombre completo
Maria Zanin
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1992
Director
Tribunal
Giacometti, José Alberto (Presidente)
Agnelli, José Augusto Marcondes
Alfaro, Renê Armando Moreno
Janiszewski, Jorge Mieczyslaw
Roda, Valentin Obac
Título en portugués
Propriedades elétricas do elastômero EPDM para aplicação em isolação elétrica
Palabras clave en portugués
Compósito
Elastômero
EPDM
Propriedades elétricas
Resumen en portugués
O objetivo deste trabalho é o de caracterizar o processo de condução do EPDM e de formulações deste material quando nele se incorpora diferentes concentrações de trihidróxido de alumínio (alumina trihidratada). Dois procedimentos experimentais foram utilizados para se obter os resultados: o primeiro utilizando medidas de corrente no estado estacionário variando-se a espessura das amostras, o potencial, o material do eletrodo e a temperatura e o segundo através de medidas da distribuição de cargas elétricas no interior do material empregando o método de propagação de um pulso de pressão. Na análise dos resultados experimentais encontrou-se presença de polarização elétrica e de condução, a qual apresenta dependência linear do logaritmo da condutividade com a raiz do campo, na região de altos campos elétricos. Estudo comparativo de alguns modelos foi realizado sem que nenhum deles explicasse os nossos resultados. Propusemos tentativamente a combinação de efeitos de superfície e de volume. Para o material com crescente concentração de alumina também se encontrou dependência da condutividade com a raiz do campo, mas a interpretação dos resultados ficou mais incerta. Além disto, um efeito quadrático com a concentração de alumina foi encontrado para a polarização e para a condução um efeito linear
Título en inglés
Electric properties of the EPDM elastomer for electrical insulation
Palabras clave en inglés
Composite
Elastomer
Electric properties
EPDM
Resumen en inglés
This work attempts to characterize the processes of electric conduction in the EPDM copolymer and its composites with several contents of alumina trihydrate filler. Two different experimental procedures were employed: (i) measurements of the steady state electric current for several sample thicknesses, applied voltages, temperatures, and different types of electrode (ii) charge distribution measurements using the pressure wave propagation method. The results showed that there is an electric polarization superimposed to an electric conduction. For high electric fields a linear dependence of the log of the conductivity versus the square root of the electric field was found. Several theoretical models were employed aimed at explaining the experimental results but none gave satisfactory results. It seems that the most adequate model is one in which both surface and bulk processes are considered. When the content of alumina trihydrate filler was increased, a linear dependence between the logs of conductivity against the square root of the electric field was again observed, though the results could not be readily interpreted. It was also found that the electric polarization and the electric conductivity show a quadratic and a linear dependence on the alumina trihydrate content, respectively
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
MariaZaninD.pdf (5.42 Mbytes)
Fecha de Publicación
2014-10-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.