Tese de Doutorado
DOI
10.11606/T.54.1992.tde-16102014-173028
Documento
Autor
Nome completo
Maria Zanin
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1992
Orientador
Banca examinadora
Giacometti, José Alberto (Presidente)
Agnelli, José Augusto Marcondes
Alfaro, Renê Armando Moreno
Janiszewski, Jorge Mieczyslaw
Roda, Valentin Obac
Título em português
Propriedades elétricas do elastômero EPDM para aplicação em isolação elétrica
Palavras-chave em português
Compósito
Elastômero
EPDM
Propriedades elétricas
Resumo em português
O objetivo deste trabalho é o de caracterizar o processo de condução do EPDM e de formulações deste material quando nele se incorpora diferentes concentrações de trihidróxido de alumínio (alumina trihidratada). Dois procedimentos experimentais foram utilizados para se obter os resultados: o primeiro utilizando medidas de corrente no estado estacionário variando-se a espessura das amostras, o potencial, o material do eletrodo e a temperatura e o segundo através de medidas da distribuição de cargas elétricas no interior do material empregando o método de propagação de um pulso de pressão. Na análise dos resultados experimentais encontrou-se presença de polarização elétrica e de condução, a qual apresenta dependência linear do logaritmo da condutividade com a raiz do campo, na região de altos campos elétricos. Estudo comparativo de alguns modelos foi realizado sem que nenhum deles explicasse os nossos resultados. Propusemos tentativamente a combinação de efeitos de superfície e de volume. Para o material com crescente concentração de alumina também se encontrou dependência da condutividade com a raiz do campo, mas a interpretação dos resultados ficou mais incerta. Além disto, um efeito quadrático com a concentração de alumina foi encontrado para a polarização e para a condução um efeito linear
Título em inglês
Electric properties of the EPDM elastomer for electrical insulation
Palavras-chave em inglês
Composite
Elastomer
Electric properties
EPDM
Resumo em inglês
This work attempts to characterize the processes of electric conduction in the EPDM copolymer and its composites with several contents of alumina trihydrate filler. Two different experimental procedures were employed: (i) measurements of the steady state electric current for several sample thicknesses, applied voltages, temperatures, and different types of electrode (ii) charge distribution measurements using the pressure wave propagation method. The results showed that there is an electric polarization superimposed to an electric conduction. For high electric fields a linear dependence of the log of the conductivity versus the square root of the electric field was found. Several theoretical models were employed aimed at explaining the experimental results but none gave satisfactory results. It seems that the most adequate model is one in which both surface and bulk processes are considered. When the content of alumina trihydrate filler was increased, a linear dependence between the logs of conductivity against the square root of the electric field was again observed, though the results could not be readily interpreted. It was also found that the electric polarization and the electric conductivity show a quadratic and a linear dependence on the alumina trihydrate content, respectively
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
MariaZaninD.pdf (5.42 Mbytes)
Data de Publicação
2014-10-20
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.