Dissertação de Mestrado
DOI
10.11606/D.54.1980.tde-27052014-151259
Documento
Autor
Nome completo
Dulcina Maria Pinatti Ferreira de Souza
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1980
Orientador
Título em português
Defeitos puntiformes em cristais de NaCl: NaF: M++
Palavras-chave em português
Cristal iônico
Defeitos puntiformes
Relaxação dielétrica
Resumo em português
Neste trabalho estudamos defeitos pontuais em cristais de NaCl + NaF contendo diversos íons divalentes e em especial o íon Pb++. As técnicas usadas foram as de I.T.C. e absorção ótica. Identificamos três novos defeitos e novos agregados de Pb++. Um modelo microscópico para os defeitos observados foi proposto. Dois dos novos picos de I.T.C. são identificados como relaxação do mesmo defeito constituído do íon divalente e um íon F- em sua proximidade. Pela primeira vez observou-se a conversão da relaxação dielétrica de um íon divalente isolado para a de uma posição perturbada. Os íons F- funcionam como armadilhas eficientes para a difusão do íon Pb++. O efeito do raio iônico sobre a relaxação desses defeitos foi observado e discutido. Atribuiu-se tentativamente a um par de vacâncias ao pico de I.T.C. de mais baixa temperatura
Título em inglês
Point Defects in NaCl : NaF : M++ crystals
Palavras-chave em inglês
Dielectric relaxation
Ionic crystal
Point defects
Resumo em inglês
This work report results on the study of point defects in NaCl + NaF single crystals doped with several divalent ions and with more details for Pb++ ions. I.T.C. and u.v. spectroscopy were the used techniques. Three new relaxation peaks were found as well as large aggregates of Pb++ and F- ions. A microscopic model for the observed defects is proposed. Two of the new I.T.C. peaks called B and C, are identified as dielectrics relaxation of one defect - its transverse and the longitudinal relaxation modes. This defect is made of one divalent ion one F anion as its close neighbor and one vacancy. For the first time it was observed the conversion of a Pb++ ion from a normal to a perturbed lattice site. The F anions are efficient traps for divalent ion diffusion. The effect of divalent ion radius on the dielectric relaxation of these perturbed defects was observed and discussed. The lower temperature peak is tentatively attributed to relaxation of a divacancy - a pair of positive and negative vacancy bound together
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
DulcinaMPinattiM.pdf (2.65 Mbytes)
Data de Publicação
2014-05-28
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.