Thèse de Doctorat
DOI
10.11606/T.58.2017.tde-14052015-110753
Document
Auteur
Nom complet
Talita Souza Dantas
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Ribeirão Preto, 2015
Directeur
Jury
Ribeiro, Ricardo Faria (Président)
Adabo, Gelson Luiz
Antunes, Rossana Pereira de Almeida
Ferracioli, Renata Cristina Silveira Rodrigues
Torres, Érica Miranda de
Titre en portugais
Comportamento mecânico, resistência de união e longevidade de pilares e coroas de zircônia obtidas por sistema CAD-CAM: influência de diferentes tratamentos de superfície
Mots-clés en portugais
Adapatação marginal
Adesão
Fadiga termomecânica
Rugosidade superficial
Tratamento de superfície
Zircônia
Resumé en portugais
O objetivo do estudo foi avaliar a resistência de união à zircônia após diferentes tratamentos de superfície e o comportamento mecânico de pilares e coroas de zircônia associados aos mesmos tratamentos. Na primeira fase, 95 discos em zircônia foram obtidos e divididos em cinco grupos (n = 19): GC (grupo controle, sem nenhum tipo de tratamento); GAL (jateamento com partículas de Al2O3 antes da sinterização); GALS (jateamento com partículas de Al2O3 após sinterização); GRO (silanização com sistema Rocatec antes da sinterização) e GROS (silanização com sistema Rocatec após sinterização). Três amostras de cada grupo tiveram a superfície analisada em MEV e MCVL. Dez amostras de cada grupo foram submetidas a ensaio de microcisalhamento e as seis restantes foram submetidas à análise de interface por meio de MEV. A análise estatística utilizou modelo de regressão linear com efeitos mistos e teste de Tukey (p < 0,01). Na segunda fase, 70 pilares do tipo hexágono externo foram obtidos em zircônia e associados a coroas totais com copings de zircônia. Os conjuntos análogo-pilar-coroa também foram divididos em cinco grupos (n=14) e submetidos aos mesmos tratamentos previamente descritos. Ainda, foram realizadas mensurações para verificação da adaptação dos copings sobre os pilares e rugosidade superficial dos discos, copings e pilares em MCVL. Foi realizado ensaio de fadiga mecânica dos conjuntos com carga progressiva de 80, 120, 160, 200, 240, 280 e 320 N, frequência de 5 Hz, totalizando 20.000 ciclos em cada estágio. A ciclagem térmica foi realizada com temperaturas entre 5º C e 55º C. Após os ensaios mecânicos, os resultados foram submetidos à análise estatística (probabilidade de sobrevida, teste de Log-Rang, p < 0,05) Os resultados apontaram que o grupo ROS apresentou valores de resistência de união significativamente superiores (p < 0,01) e que a rugosidade superficial foi semelhante para discos e copings (p = 0,22) e para discos e pilares (p = 0,96), e diferente entre copings e pilares (p < 0,01). A desadaptação marginal foi maior para o grupo RO (p < 0,01) e a probabilidade de sobrevida dos conjuntos foi similar para todos os grupos testados (p = 0,57). Concluiu-se que a utilização do Rocatec aumenta os valores de resistência de união à zircônia, não compromete o comportamento mecânico do material e sua utilização é viável em peças já sinterizadas.
Titre en anglais
Mechanical behavior, bond strength and reliability of YTZP abutments and crowns processed by CAD/CAM: The role of surface treatments
Mots-clés en anglais
Adhesion
Marginal gap
Surface roughness
Surface treatment
Thermomechanical fatigue
Zirconia
Resumé en anglais
The aim of this study was to evaluate the bond strength to zirconia after different surface treatments and to evaluate the mechanical behavior of zirconia abutments and crowns associated with these treatments. In the first phase, 95 discs in zirconia were obtained and divided into five groups (n = 19): GC (control group, without any treatment), GAL (air particle abrasion with Al2O3 particles before sintering), GALS (air particle abrasion with Al2O3 particles after sintering), GRO (silanization with Rocatec system before sintering) and GROS (silanization with Rocatec system after sintering). Three samples of each group had the surfaces analyzed in SEM and CLSM. Ten samples of each group were subjected to microshear test and the other remaining six had their interface examined by SEM. The statistical analysis used a linear regression model with mixed effects and Tukey test (p <0.01). In the second stage, 70 external hex abutments were obtained in zirconia and associated with crowns and zirconia copings. The analog-abutment-crown assemblies were also divided into five groups (n = 14) and subjected to the same treatments described previously. Measurements to verify the adaptation of copings on the abutments and surface roughness of the discs, copings and abutments were performed in CLSM. A fatigue test was carried with progressive load of 80, 120, 160, 200, 240, 280 and 320 N, frequency of 5 Hz and 20,000 cycles at each stage. Thermal cycling was performed with temperatures between 5° C and 55° C. After mechanical tests, the results were subjected to statistical analysis (survival probability, Log-Rang test, p <0.05) The results showed that the ROS group had significantly higher bond strength values (p < 0.01) and that the surface roughness was similar for discs and copings (p = 0.22) and for discs and abutments (p = 0.96), and was different between copings and abutments (p < 0.01). The marginal gap was higher for RO group (p < 0.01) and the survival probability of the sets was similar for all tested groups (p = 0.57). It was concluded that the use of Rocatec increases the bond strength values to zirconia, does not compromise the mechanical behavior of the material and its use is now feasible in sintered parts.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2017-08-16
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.